- 熔体流动速率 [g/10min]: 1.9
- 密度 [g/cm3]: 1.78
- 拉伸强度 [MPa]: 20.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.78 g/cc | 0.0643 lb/in³ | |
Melt Flow | 1.9 g/10 min @Load 5.00 kg, Temperature 230 °C | 1.9 g/10 min @Load 11.0 lb, Temperature 446 °F | |
Mechanical Properties | Metric | English | Comments |
Tensile Strength, Yield | 20.0 MPa | 2900 psi | 50 mm/min |
Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
Elongation at Yield | 16 % | 16 % | 50 mm/min |
Tensile Modulus | 0.480 GPa | 69.6 ksi | 1 mm/min |
Charpy Impact, Notched | 11.8 J/cm² | 56.2 ft-lb/in² | |
0.600 J/cm² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | ||
Electrical Properties | Metric | English | Comments |
Electrical Resistivity | 2.00e+14 ohm-cm | 2.00e+14 ohm-cm | |
Dielectric Constant | 7.1 @Frequency 1e+6 Hz | 7.1 @Frequency 1e+6 Hz | |
11.4 @Frequency 100 Hz | 11.4 @Frequency 100 Hz | ||
Dissipation Factor | 0.024 @Frequency 100 Hz | 0.024 @Frequency 100 Hz | |
Thermal Properties | Metric | English | Comments |
CTE, linear, Parallel to Flow | 177 µm/m-°C @Temperature 20.0 °C | 98.3 µin/in-°F @Temperature 68.0 °F | |
Melting Point | 135 °C | 275 °F | 10°C/min |
Vicat Softening Point | 61.0 °C | 142 °F | 50°C/hr; 50N |
Glass Transition Temp, Tg | -34.0 °C | -29.2 °F | 10°C/min |
Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |
V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | ||
Oxygen Index | 49 % | 49 % |