- 吸水率 [%]: 0.03
- 缺口冲击强度: 6.41
- 拉伸强度 [MPa]: 20.0
- 弯曲强度 [MPa]: 24.1
- 弯曲模量 [MPa]: 0.621
- 热变形温度 [℃]: 60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.76 - 1.79 g/cc | 1.76 - 1.79 g/cc | ASTM D792 |
| Water Absorption | 0.030 - 0.050 % | 0.030 - 0.050 % | 24 hr / 20°C; ASTM D570 |
| Ash | 0.00 - 5.0 % | 0.00 - 5.0 % | Thermal Decomposition/ in air |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 - 70 | 65 - 70 | ASTM D2240 |
| Tensile Strength, Ultimate | 24.1 - 41.4 MPa | 3500 - 6000 psi | ASTM D638 |
| Tensile Strength, Yield | 20.0 - 27.6 MPa | 2900 - 4000 psi | ASTM D638 |
| Elongation at Break | 200 - 400 % | 200 - 400 % | ASTM D638 |
| Elongation at Yield | 10 - 20 % | 10 - 20 % | ASTM D638 |
| Tensile Modulus | 0.552 - 0.896 GPa | 80.0 - 130 ksi | ASTM D638 |
| Flexural Strength | 20.7 - 34.5 MPa | 3000 - 5000 psi | @ 5% strain; ASTM D790 |
| Flexural Modulus | 0.621 - 0.827 GPa | 90.0 - 120 ksi | ASTM D790 |
| Compressive Strength | 31.0 - 41.4 MPa | 4500 - 6000 psi | ASTM D695 |
| Izod Impact, Notched | 6.41 - 10.7 J/cm | 12.0 - 20.0 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.33 | 0.33 | vs. Steel; ASTM D1894 |
| Coefficient of Friction, Static | 0.33 | 0.33 | vs. Steel; ASTM D1894 |
| Taber Abrasion, mg/1000 Cycles | 16 - 19 | 16 - 19 | CS-17 1000g:load |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+14 ohm-cm | 2.00e+14 ohm-cm | DC, 65% RH; ASTM D257 |
| Dielectric Constant | 3.5 - 4.3 @Frequency 1e+8 Hz | 3.5 - 4.3 @Frequency 1e+8 Hz | ASTM D150 |
| 9.4 - 10.6 @Frequency 100 Hz | 9.4 - 10.6 @Frequency 100 Hz | ASTM D150 | |
| Dielectric Strength | 51.2 - 59.1 kV/mm | 1300 - 1500 kV/in | ASTM D149 |
| Dissipation Factor | 0.090 - 0.14 @Frequency 100 Hz | 0.090 - 0.14 @Frequency 100 Hz | ASTM D150 |
| 0.19 - 0.21 @Frequency 1e+8 Hz | 0.19 - 0.21 @Frequency 1e+8 Hz | ASTM D150 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 126 - 185 µm/m-°C @Temperature 20.0 °C | 70.0 - 103 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Specific Heat Capacity | 1.17 - 1.51 J/g-°C | 0.280 - 0.360 BTU/lb-°F | DSC |
| Thermal Conductivity | 0.144 - 0.180 W/m-K | 1.00 - 1.25 BTU-in/hr-ft²-°F | ASTM D433 |
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 - 75.0 °C | 140 - 167 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 40.0 - 55.0 °C | 104 - 131 °F | ASTM D648 |
| Glass Transition Temp, Tg | -42.0 - -39.0 °C | -43.6 - -38.2 °F | (DMA) @ 1 Hz |
| Decomposition Temperature | 375 °C | 707 °F | 1% wt. loss / in air |
| 410 °C | 770 °F | 1% wt. loss / in nitrogen | |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 42 % | 42 % | Limiting, (Optional product available with higher value of 95% O2; ASTM D2868 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.41 @Temperature 25.0 °C, Wavelength 589.3 nm | 1.41 @Temperature 77.0 °F, Wavelength 589.3 nm | Sodium D line; ASTM D542 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 141 - 145 °C | 285 - 293 °F | ASTM D3418 |