- 熔体流动速率 [g/10min]: 4.5
- 密度 [g/cm3]: 1.78
- 吸水率 [%]: 0.03
- 拉伸强度 [MPa]: 52.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.78 g/cc | 0.0643 lb/in³ | |
| Water Absorption | 0.030 % | 0.030 % | |
| Moisture Absorption at Equilibrium | 0.015 % | 0.015 % | Humidity Absorption |
| Melt Flow | 4.5 g/10 min @Load 5.00 kg, Temperature 230 °C | 4.5 g/10 min @Load 11.0 lb, Temperature 446 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 9.0 % | 9.0 % | 50 mm/min |
| Tensile Modulus | 2.20 GPa | 319 ksi | 1 mm/min |
| Charpy Impact Unnotched | 25.5 J/cm² | 121 ft-lb/in² | |
| 22.2 J/cm² @Temperature -30.0 °C | 106 ft-lb/in² @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | |
| 0.500 J/cm² @Temperature -30.0 °C | 2.38 ft-lb/in² @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 7.2 @Frequency 1e+6 Hz | 7.2 @Frequency 1e+6 Hz | |
| 9.9 @Frequency 100 Hz | 9.9 @Frequency 100 Hz | ||
| Dissipation Factor | 0.030 @Frequency 100 Hz | 0.030 @Frequency 100 Hz | |
| 0.226 @Frequency 1e+6 Hz | 0.226 @Frequency 1e+6 Hz | ||
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 150 µm/m-°C @Temperature 20.0 °C | 83.3 µin/in-°F @Temperature 68.0 °F | |
| Melting Point | 171 °C | 340 °F | 10°C/min |
| Deflection Temperature at 1.8 MPa (264 psi) | 107 °C | 225 °F | |
| Vicat Softening Point | 139 °C | 282 °F | 50°C/hr; 50N |
| Glass Transition Temp, Tg | -40.0 °C | -40.0 °F | 10°C/min |
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | |
| V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | ||
| Oxygen Index | 80.7 % | 80.7 % | |