- 熔体流动速率 [g/10min]: 4.0
- 吸水率 [%]: 0.03
- 拉伸强度 [MPa]: 14.0
- 弯曲模量 [MPa]: 0.276
- 热变形温度 [℃]: 49.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.78 - 1.80 g/cc | 1.78 - 1.80 g/cc | ASTM D792 |
| Bulk Density | 0.961 g/cc | 0.0347 lb/in³ | |
| Water Absorption | 0.030 - 0.060 % @Time 86400 sec | 0.030 - 0.060 % @Time 24.0 hour | Immersion; ASTM D570 |
| Viscosity | 2.00e+6 - 2.50e+6 cP @Shear Rate 100 1/s, Temperature 232 °C | 2.00e+6 - 2.50e+6 cP @Shear Rate 100 1/s, Temperature 450 °F | Melt Viscosity; ASTM D3835 |
| Melt Flow | 4.0 - 14 g/10 min @Load 12.5 kg, Temperature 232 °C | 4.0 - 14 g/10 min @Load 27.6 lb, Temperature 450 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 57 - 62 | 57 - 62 | ASTM D2240 |
| Tensile Strength at Break | 20.0 - 27.0 MPa | 2900 - 3920 psi | ASTM D638 |
| Tensile Strength, Yield | 14.0 - 21.0 MPa | 2030 - 3050 psi | ASTM D638 |
| Elongation at Break | 200 - 400 % | 200 - 400 % | ASTM D638 |
| Elongation at Yield | 15 - 25 % | 15 - 25 % | ASTM D638 |
| Tensile Modulus | 0.276 - 0.448 GPa | 40.0 - 65.0 ksi | ASTM D638 |
| Flexural Strength | 14.0 - 24.0 MPa @Strain 5.00 % | 2030 - 3480 psi @Strain 5.00 % | ASTM D790 |
| Flexural Modulus | 0.276 - 0.414 GPa | 40.0 - 60.0 ksi | ASTM D790 |
| Compressive Strength | 24.0 - 31.0 MPa | 3480 - 4500 psi | ASTM D695 |
| Izod Impact, Notched | >= NB | >= NB | ASTM D256 |
| Izod Impact, Unnotched | >= NB | >= NB | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.54 | 0.54 | vs. steel; ASTM D1894 |
| Coefficient of Friction, Static | 0.55 | 0.55 | vs. steel; ASTM D1894 |
| Taber Abrasion, mg/1000 Cycles | 21 - 25 | 21 - 25 | 1000 g pad; CS-17 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+14 ohm-cm @Temperature 20.0 °C | 2.00e+14 ohm-cm @Temperature 68.0 °F | 65% RH; ASTM D257 |
| Dielectric Constant | 3.8 @Frequency 1.00e+8 Hz | 3.8 @Frequency 1.00e+8 Hz | ASTM D150 |
| 12.1 @Frequency 100 Hz | 12.1 @Frequency 100 Hz | ASTM D150 | |
| Dielectric Strength | 43.3 - 51.2 kV/mm | 1100 - 1300 kV/in | ASTM D149 |
| Dissipation Factor | 0.020 - 0.24 @Frequency 100 Hz | 0.020 - 0.24 @Frequency 100 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 162 - 216 µm/m-°C | 90.0 - 120 µin/in-°F | ASTM D696 |
| Specific Heat Capacity | 1.17 - 1.51 J/g-°C | 0.280 - 0.360 BTU/lb-°F | DSC |
| Thermal Conductivity | 0.144 - 0.180 W/m-K | 1.00 - 1.25 BTU-in/hr-ft²-°F | ASTM D433 |
| Melting Point | 130 - 138 °C | 266 - 280 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 49.0 - 65.0 °C | 120 - 149 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 35.0 - 51.0 °C | 95.0 - 124 °F | ASTM D648 |
| Glass Transition Temp, Tg | -42.0 - -40.0 °C @Frequency 1.00 Hz | -43.6 - -40.0 °F @Frequency 1.00 Hz | DMA |
| Decomposition Temperature | 375 °C | 707 °F | 1% wt loss / in air; TGA |
| 410 °C | 770 °F | 1% wt loss / in nitrogen; TGA | |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 43 % | 43 % | ASTM D2868 |
| 95 % | 95 % | optional products; ASTM D2868 | |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 195 - 220 °C | 383 - 428 °F | Tube Extrusion |
| 200 - 220 °C | 392 - 428 °F | Injection Molding | |
| Middle Barrel Temperature | 210 - 230 °C | 410 - 446 °F | Injection Molding |
| 220 - 240 °C | 428 - 464 °F | Tube Extrusion | |
| Front Barrel Temperature | 220 - 250 °C | 428 - 482 °F | Tube Extrusion |
| 220 - 250 °C | 428 - 482 °F | Injection Molding | |
| Nozzle Temperature | 210 - 245 °C | 410 - 473 °F | Injection Molding |
| Die Temperature | 220 - 250 °C | 428 - 482 °F | Tube Extrusion |
| Head Temperature | 220 - 250 °C | 428 - 482 °F | Tube Extrusion |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | Injection Molding |