- 熔体流动速率 [g/10min]: 2.8
- 拉伸强度 [MPa]: 53.0
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Specific Gravity | 1.75 - 1.80 g/cc | 1.75 - 1.80 g/cc | ASTM D792 | ||
Water Absorption | <= 0.040 % @Temperature 23.0 °C, Time 86400 sec | <= 0.040 % @Temperature 73.4 °F, Time 24.0 hour | ASTM D570 | ||
Melt Flow | 2.8 - 4.6 g/10 min @Load 21.6 kg, Temperature 230 °C | 2.8 - 4.6 g/10 min @Load 47.6 lb, Temperature 446 °F | ASTM D1238 | ||
Mechanical Properties | Metric | English | Comments | ||
Tensile Strength at Break | 35.0 - 50.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C | 5080 - 7250 psi @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
Tensile Strength, Yield | 53.0 - 57.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C | 7690 - 8270 psi @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
Elongation at Break | 20 - 50 % @Thickness 2.00 mm, Temperature 23.0 °C | 20 - 50 % @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
Elongation at Yield | 5.0 - 10 % @Thickness 2.00 mm, Temperature 23.0 °C | 5.0 - 10 % @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
Tensile Modulus | 2.10 - 2.30 GPa @Thickness 2.00 mm, Temperature 23.0 °C | 305 - 334 ksi @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 1.0 mm/min; ASTM D638 | ||
Thermal Properties | Metric | English | Comments | ||
Heat of Fusion | 50.0 - 56.0 J/g | 21.5 - 24.1 BTU/lb | Crystallization Heat; ASTM D3417 | ||
57.0 - 66.0 J/g | 24.5 - 28.4 BTU/lb | ASTM D3417 | |||
Melting Point | 171 - 175 °C | 340 - 347 °F | ASTM D3418 | ||
Crystallization Temperature | 137 - 144 °C | 279 - 291 °F | Peak, DSC; ASTM D3418 | ||
Glass Transition Temp, Tg | -40.0 °C | -40.0 °F | ASTM D4065 | ||
Descriptive Properties | |||||
Availability | Africa & Middle East | ||||
Asia Pacific | |||||
Europe | |||||
North America | |||||
South America | |||||
Features | Homopolymer | ||||
Very high Viscosity | |||||
Forms | Powder | ||||
Generic | PVDF | ||||
Uses | Membranes |