- 密度 [g/cm3]: 0.7
- 缺口冲击强度: 1.3
- 拉伸强度 [MPa]: 0.862
- 断裂伸长率 [%]: 14.0
- 弯曲强度 [MPa]: 13.0
- 弯曲模量 [MPa]: 0.490
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.700 - 3.35 g/cc | 0.0253 - 0.121 lb/in³ | Average value: 2.07 g/cc Grade Count:103 |
| Apparent Bulk Density | 0.360 - 0.950 g/cc | 0.0130 - 0.0343 lb/in³ | Average value: 0.667 g/cc Grade Count:26 |
| Water Absorption | 0.000 - 0.100 % | 0.000 - 0.100 % | Average value: 0.00640 % Grade Count:55 |
| Particle Size | 25.0 - 4450 µm | 25.0 - 4450 µm | Average value: 481 µm Grade Count:26 |
| Viscosity | 1.00e+13 - 1.00e+15 cP @Temperature 340 - 380 °C | 1.00e+13 - 1.00e+15 cP @Temperature 644 - 716 °F | Average value: 5.05e+14 cP Grade Count:12 |
| Linear Mold Shrinkage | 0.0200 - 0.0500 cm/cm | 0.0200 - 0.0500 in/in | Average value: 0.0321 cm/cm Grade Count:28 |
| Deformation | 0.200 - 17.0 % | 0.200 - 17.0 % | Average value: 6.41 % Grade Count:30 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 11.0 - 70.0 | 11.0 - 70.0 | Average value: 57.0 Grade Count:37 |
| Ball Indentation Hardness | 23.0 - 37.0 MPa | 3340 - 5370 psi | Average value: 32.0 MPa Grade Count:9 |
| Tensile Strength, Ultimate | 13.0 - 333 MPa | 1890 - 48300 psi | Average value: 34.1 MPa Grade Count:53 |
| Tensile Strength, Yield | 0.862 - 41.4 MPa | 125 - 6000 psi | Average value: 20.5 MPa Grade Count:49 |
| Elongation at Break | 40.0 - 650 % | 40.0 - 650 % | Average value: 293 % Grade Count:103 |
| Modulus of Elasticity | 0.392 - 2.25 GPa | 56.9 - 326 ksi | Average value: 0.556 GPa Grade Count:42 |
| Flexural Yield Strength | 14.0 - 27.6 MPa | 2030 - 4000 psi | Average value: 19.6 MPa Grade Count:3 |
| Flexural Modulus | 0.490 - 3.34 GPa | 71.1 - 485 ksi | Average value: 0.736 GPa Grade Count:15 |
| Compressive Yield Strength | 1.50 - 23.4 MPa | 218 - 3400 psi | Average value: 7.20 MPa Grade Count:23 |
| Shear Strength | 9.30792 - 25.5106 MPa @Temperature 26.7 - 204 °C | 1350.00 - 3700.01 psi @Temperature 80.0 - 400 °F | Average value: 15.1 MPa Grade Count:2 |
| Izod Impact, Notched | 1.30 - 1.57 J/cm | 2.44 - 2.94 ft-lb/in | Average value: 1.42 J/cm Grade Count:7 |
| Izod Impact, Unnotched | 1.60 J/cm | 3.00 ft-lb/in | Average value: 1.60 J/cm Grade Count:12 |
| Charpy Impact, Notched | 1.40 - 1.90 J/cm² | 6.66 - 9.04 ft-lb/in² | Average value: 1.76 J/cm² Grade Count:5 |
| Coefficient of Friction | 0.0200 - 0.280 | 0.0200 - 0.280 | Average value: 0.0604 Grade Count:42 |
| Coefficient of Friction, Static | 0.0200 - 0.0800 | 0.0200 - 0.0800 | Average value: 0.0530 Grade Count:30 |
| K (wear) Factor | 3.00 - 5040 x 10-8 mm³/N-M | 1.49 - 2500 x 10-10 in³-min/ft-lb-hr | Average value: 1920 x 10-8 mm³/N-M Grade Count:7 |
| Taber Abrasion, mg/1000 Cycles | 15.8 - 41.8 | 15.8 - 41.8 | Average value: 26.1 Grade Count:12 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 - 1.10e+18 ohm-cm | 1.00e+14 - 1.10e+18 ohm-cm | Average value: 8.42e+17 ohm-cm Grade Count:41 |
| Surface Resistance | 1.00e+13 - 1.00e+18 ohm | 1.00e+13 - 1.00e+18 ohm | Average value: 3.88e+17 ohm Grade Count:12 |
| Dielectric Constant | 2.00 - 12.0 | 2.00 - 12.0 | Average value: 2.42 Grade Count:48 |
| Dielectric Strength | 2.50 - 165 kV/mm | 63.5 - 4200 kV/in | Average value: 57.6 kV/mm Grade Count:65 |
| Dissipation Factor | 0.0000100 - 0.0360 | 0.0000100 - 0.0360 | Average value: 0.00120 Grade Count:51 |
| Arc Resistance | 300 - 420 sec | 300 - 420 sec | Average value: 400 sec Grade Count:6 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:6 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 14.0 - 250 µm/m-°C | 7.78 - 139 µin/in-°F | Average value: 107 µm/m-°C Grade Count:46 |
| 57.0 - 170 µm/m-°C @Temperature 30.0 - 300 °C | 31.7 - 94.4 µin/in-°F @Temperature 86.0 - 572 °F | Average value: 95.7 µm/m-°C Grade Count:9 | |
| Specific Heat Capacity | 1.00 - 1.05 J/g-°C | 0.239 - 0.251 BTU/lb-°F | Average value: 1.01 J/g-°C Grade Count:6 |
| 0.960 - 1.03 J/g-°C @Temperature 0.000 - 50.0 °C | 0.229 - 0.246 BTU/lb-°F @Temperature 32.0 - 122 °F | Average value: 0.995 J/g-°C Grade Count:1 | |
| Thermal Conductivity | 0.230 - 0.500 W/m-K | 1.60 - 3.47 BTU-in/hr-ft²-°F | Average value: 0.261 W/m-K Grade Count:39 |
| 0.220 - 0.320 W/m-K @Temperature 100 - 250 °C | 1.53 - 2.22 BTU-in/hr-ft²-°F @Temperature 212 - 482 °F | Average value: 0.276 W/m-K Grade Count:7 | |
| Melting Point | 135 - 340 °C | 275 - 644 °F | Average value: 323 °C Grade Count:46 |
| Maximum Service Temperature, Air | 93.3 - 316 °C | 200 - 600 °F | Average value: 260 °C Grade Count:69 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 - 93.3 °C | 122 - 200 °F | Average value: 64.8 °C Grade Count:3 |
| Minimum Service Temperature, Air | -268 - -200 °C | -450 - -328 °F | Average value: -215 °C Grade Count:19 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:57 |
| Oxygen Index | 92.0 - 95.0 % | 92.0 - 95.0 % | Average value: 94.9 % Grade Count:28 |
| Shrinkage | 2.50 - 5.80 % | 2.50 - 5.80 % | Average value: 3.96 % Grade Count:7 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 370 °C | 698 °F | Average value: 370 °C Grade Count:5 |
| Back Pressure | 15.0 - 40.0 MPa | 2180 - 5800 psi | Average value: 27.5 MPa Grade Count:5 |