- 密度 [g/cm3]: 2.28
- 缺口冲击强度: 1.08
- 拉伸强度 [MPa]: 14.0
- 弯曲强度 [MPa]: 3.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.28 - 4.00 g/cc | 0.0824 - 0.145 lb/in³ | Average value: 3.52 g/cc Grade Count:26 |
| Filler Content | 30.0 - 60.0 % | 30.0 - 60.0 % | Average value: 43.3 % Grade Count:3 |
| Apparent Bulk Density | 0.930 - 1.30 g/cc | 0.0336 - 0.0470 lb/in³ | Average value: 1.06 g/cc Grade Count:3 |
| Particle Size | 40.0 - 740 µm | 40.0 - 740 µm | Average value: 316 µm Grade Count:5 |
| Linear Mold Shrinkage | 0.0180 - 0.0190 cm/cm | 0.0180 - 0.0190 in/in | Average value: 0.0183 cm/cm Grade Count:3 |
| Deformation | 1.40 - 11.0 % | 1.40 - 11.0 % | Average value: 5.56 % Grade Count:15 |
| 1.00 - 11.0 % @Temperature 150 - 150 °C | 1.00 - 11.0 % @Temperature 302 - 302 °F | Average value: 5.55 % Grade Count:2 | |
| 1.00 - 11.0 % @Pressure 0.981 - 4.90 MPa | 1.00 - 11.0 % @Pressure 142 - 711 psi | Average value: 5.55 % Grade Count:2 | |
| 1.00 - 11.0 % @Time 86400 - 86400 sec | 1.00 - 11.0 % @Time 24.0 - 24.0 hour | Average value: 5.55 % Grade Count:2 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 56.0 - 72.0 | 56.0 - 72.0 | Average value: 63.7 Grade Count:23 |
| Ball Indentation Hardness | 36.0 - 60.0 MPa | 5220 - 8700 psi | Average value: 48.6 MPa Grade Count:10 |
| Tensile Strength, Ultimate | 3.00 - 28.0 MPa | 435 - 4060 psi | Average value: 17.6 MPa Grade Count:23 |
| Tensile Strength, Yield | 14.0 - 20.0 MPa | 2030 - 2900 psi | Average value: 16.6 MPa Grade Count:5 |
| Elongation at Break | 3.00 - 310 % | 3.00 - 310 % | Average value: 182 % Grade Count:28 |
| Compressive Yield Strength | 6.50 - 20.0 MPa | 943 - 2900 psi | Average value: 11.4 MPa Grade Count:9 |
| Izod Impact, Notched | 1.08 - 1.40 J/cm | 2.02 - 2.62 ft-lb/in | Average value: 1.29 J/cm Grade Count:4 |
| Coefficient of Friction | 0.0600 - 0.230 | 0.0600 - 0.230 | Average value: 0.143 Grade Count:16 |
| Coefficient of Friction, Static | 0.0600 - 0.300 | 0.0600 - 0.300 | Average value: 0.145 Grade Count:12 |
| K (wear) Factor | 9.00 - 32.0 x 10-8 mm³/N-M | 4.47 - 15.9 x 10-10 in³-min/ft-lb-hr | Average value: 16.4 x 10-8 mm³/N-M Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 10000 - 8.10e+16 ohm-cm | 10000 - 8.10e+16 ohm-cm | Average value: 6.23e+15 ohm-cm Grade Count:13 |
| Surface Resistance | 10000 - 5.50e+16 ohm | 10000 - 5.50e+16 ohm | Average value: 6.88e+15 ohm Grade Count:8 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 65.0 - 180 µm/m-°C | 36.1 - 100 µin/in-°F | Average value: 103 µm/m-°C Grade Count:13 |
| 70.0 - 130 µm/m-°C @Temperature 30.0 - 300 °C | 38.9 - 72.2 µin/in-°F @Temperature 86.0 - 572 °F | Average value: 100 µm/m-°C Grade Count:2 | |
| Thermal Conductivity | 0.350 - 0.965 W/m-K | 2.43 - 6.69 BTU-in/hr-ft²-°F | Average value: 0.717 W/m-K Grade Count:8 |
| Melting Point | 327 - 330 °C | 621 - 626 °F | Average value: 327 °C Grade Count:11 |
| Maximum Service Temperature, Air | 260 - 300 °C | 500 - 572 °F | Average value: 264 °C Grade Count:17 |
| Minimum Service Temperature, Air | -260 - -50.0 °C | -436 - -58.0 °F | Average value: -161 °C Grade Count:15 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:10 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 360 °C | 680 °F | Average value: 360 °C Grade Count:3 |
| Back Pressure | 40.0 - 80.0 MPa | 5800 - 11600 psi | Average value: 60.0 MPa Grade Count:3 |