- 密度 [g/cm3]: 2.05
- 断裂伸长率 [%]: 10.3
- 弯曲模量 [MPa]: 1.09
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 2.05 - 2.13 g/cc | 0.0741 - 0.0770 lb/in³ | BS2782:Pt6 | ||
| Deformation | 4.8 % @Time 3600 sec, Pressure 14.2 MPa | 4.8 % @Time 1.00 hour, Pressure 2060 psi | ASTM D621 | ||
| 6.6 % @Pressure 14.2 MPa, Time 86400 sec | 6.6 % @Pressure 2060 psi, Time 24.0 hour | ASTM D621 | |||
| 6.6 % @Time 3600 sec, Pressure 5.00 MPa | 6.6 % @Time 1.00 hour, Pressure 725 psi | 150°C; ASTM D621 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 70 - 72 | 70 - 72 | ASTM D2240 | ||
| Tensile Strength | 12.0 - 25.0 MPa | 1740 - 3630 psi | Moulding Direction; BS2782:Pt3 | ||
| Elongation at Break | 50 - 250 % | 50 - 250 % | Moulding Direction; BS2782:Pt3 | ||
| Flexural Yield Strength | 10.3 MPa @Strain 0.200 % | 1490 psi @Strain 0.200 % | ASTM D790 | ||
| Flexural Modulus | 1.09 GPa | 158 ksi | ASTM D790 | ||
| Compressive Strength | 2.30 MPa @Strain 0.200 %, Temperature 150 °C | 334 psi @Strain 0.200 %, Temperature 302 °F | ASTM D695 | ||
| 9.13 MPa @Strain 0.200 %, Temperature 23.0 °C | 1320 psi @Strain 0.200 %, Temperature 73.4 °F | ASTM D695 | |||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 0.580 W/m-K | 4.03 BTU-in/hr-ft²-°F | Moulding Direction; ASTM C177 | ||
| Melting Point | 327 °C | 621 °F | ASTM D3417 | ||
| Maximum Service Temperature, Air | 260 °C | 500 °F | |||
| 300 °C | 572 °F | Short Periods | |||
| Minimum Service Temperature, Air | -200 °C | -328 °F | |||
| Flash Point | 630 °C | 1170 °F | ASTM D1929 | ||
| Oxygen Index | 98 - 100 % | 98 - 100 % | ASTM D2863 | ||
| Descriptive Properties | |||||
| Color | Black | ||||