- 密度 [g/cm3]: 2.15
- 弯曲强度 [MPa]: 20.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.15 g/cc | 0.0777 lb/in³ | Sintered moldings; ASTM D4894/D4895 |
| Apparent Bulk Density | 0.760 g/cc | 0.0275 lb/in³ | DIN 53 466 |
| Linear Mold Shrinkage | 0.050 cm/cm @Thickness 80.0 mm | 0.050 in/in @Thickness 3.15 in | sheet; ASTM D4894 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 63 | 63 | ASTM D2240 |
| Tensile Strength, Ultimate | 20.0 MPa @Thickness 2.00 mm | 2900 psi @Thickness 0.0787 in | ASTM D4894 |
| Elongation at Break | 350 % @Thickness 2.00 mm | 350 % @Thickness 0.0787 in | ASTM D4894 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 10000 ohm-cm | 10000 ohm-cm | IEC 60093 |
| Surface Resistance | 10000 ohm | 10000 ohm | IEC 60093 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 160 µm/m-°C @Temperature 30.0 - 200 °C | 88.9 µin/in-°F @Temperature 86.0 - 392 °F | |
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | DIN 52 612 |