- 密度 [g/cm3]: 2.17
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.17 g/cc | 0.0784 lb/in³ | ASTM 1457-62 T |
| Deformation | 7.0 % | 7.0 % | 14 MPa, 100 h, 23°C; ASTM D621-59 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 32.0 MPa | 4640 psi | ASTM 1457-62 T |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM 1457-62 T |
| Elongation at Break | 160 % | 160 % | ASTM 1457-62 T |
| Coefficient of Friction, Dynamic | 0.18 - 0.22 | 0.18 - 0.22 | v = 1 m/s |
| 0.20 - 0.23 | 0.20 - 0.23 | v = 1.9 m/s | |
| Abrasion | 4.0 | 4.0 | mm of depth after 70 hrs load duration; Partner Material ST 50 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | DIN 53482 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 110 µm/m-°C @Temperature 100 °C | 61.1 µin/in-°F @Temperature 212 °F | DIN 52328 |
| Thermal Conductivity | 0.930 W/m-K | 6.45 BTU-in/hr-ft²-°F | DIN 52612 |