- 熔体流动速率 [g/10min]: 2.0
- 吸水率 [%]: 0.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D1505 |
| Water Absorption | 0.80 % | 0.80 % | Extractable Content |
| 1.4 % | 1.4 % | in 24 hours | |
| Moisture Absorption at Equilibrium | 2.5 % | 2.5 % | at 50% RH |
| Water Absorption at Saturation | 9.0 % | 9.0 % | |
| Oxygen Transmission Rate | 37.2 cc/m²/day | 2.40 cc/100 in²/day | |
| Nitrogen Transmission | 7.80 cc-mm/m²-24hr-atm | 19.8 cc-mil/100 in²-24hr-atm | cc/m²/day, No thickness given |
| Carbon Dioxide Transmission | 113 cc-mm/m²-24hr-atm | 287 cc-mil/100 in²-24hr-atm | cc/m²/day, No thickness given |
| Viscosity Measurement | 3.55 | 3.55 | 96% SAV |
| 115 | 115 | FAV; ASTM D789 | |
| Maximum Moisture Content | 0.080 | 0.080 | |
| Melt Flow | 2.0 g/10 min @Load 1.00 kg, Temperature 235 °C | 2.0 g/10 min @Load 2.20 lb, Temperature 455 °F | ASTM D1238 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 200 °C | 392 °F | ASTM D3418 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 225 - 245 °C | 437 - 473 °F | Tubular (Blown) Film |
| 225 - 250 °C | 437 - 482 °F | Cast Film | |
| Adapter Temperature | 243 °C | 469 °F | Tubular (Blown) Film |
| 250 °C | 482 °F | Cast Film | |
| Die Temperature | 240 °C | 464 °F | Cast Film |
| 240 °C | 464 °F | Tubular (Blown) Film | |
| Melt Temperature | 243 °C | 469 °F | Tubular (Blown) Film |
| 248 °C | 478 °F | Cast Film | |
| Moisture Content | 0.080 % | 0.080 % | |