- 熔体流动速率 [g/10min]: 188.38
- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 8.0
- 缺口冲击强度: 11.0
- 拉伸强度 [MPa]: 45.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 | ||
| Water Absorption | 8.0 - 9.0 % | 8.0 - 9.0 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.6 - 3.2 % | 2.6 - 3.2 % | 23°C; 50% RH; ISO 62 | ||
| Viscosity Measurement | 150 | 150 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | restricted | ||
| Melt Flow | 188.38 g/10 min @Load 5.00 kg, Temperature 275 °C | 188.38 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 20 % | 20 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 1.50 GPa | 218 ksi | ISO 527-1/-2 | ||
| Izod Impact, Notched (ISO) | 11.0 kJ/m² @Temperature 23.0 °C | 5.23 ft-lb/in² @Temperature 73.4 °F | ISO 180/A | ||
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 3.50 J/cm² @Temperature 23.0 °C | 16.7 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Tensile Creep Modulus, 1000 hours | 890 MPa @Strain <=0.500 % | 129000 psi @Strain <=0.500 % | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+9 ohm-cm | 1.00e+9 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+10 ohm | >= 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Constant | 6.0 @Frequency 1.00 Hz | 6.0 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.30 @Frequency 1.00e+6 Hz | 0.30 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Transverse to Flow | 60.0 - 100 µm/m-°C @Temperature 23.0 - 80.0 °C | 33.3 - 55.6 µin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| Specific Heat Capacity | 1.70 J/g-°C | 0.406 BTU/lb-°F | |||
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 243 °C | 469 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 107 °C | 225 °F | for 50% loss of tensile strength after 20000hr | ||
| 123 °C | 253 °F | for 50% loss of tensile strength after 5000hr | |||
| 200 °C | 392 °F | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Color | BK 23079 | ||||
| Commercial Status | Europe | ||||