- 熔体流动速率 [g/10min]: 82.5
- 密度 [g/cm3]: 1.1
- 热变形温度 [℃]: 57.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in³ | |||
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 4.5 - 5.0 % | 4.5 - 5.0 % | ISO 62 | ||
| Viscosity Measurement | 125 | 125 | ISO 307 | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm | 0.0030 in/in | ISO 2577 | ||
| Melt Flow | 82.5 g/10 min @Load 10.0 kg, Temperature 230 °C | 82.5 g/10 min @Load 22.0 lb, Temperature 446 °F | ISO 1133 | ||
| 132 g/10 min @Load 5.00 kg, Temperature 275 °C | 132 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 85 | 85 | ISO 868 | ||
| Elongation at Yield | 5.0 % | 5.0 % | 50mm/min; ISO 527-1/-2 | ||
| Tensile Modulus | 2.50 GPa | 363 ksi | ISO 527-1/-2 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 0.800 - 1.20 µm/m-°C @Temperature 23.0 - 55.0 °C | 0.444 - 0.667 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 0.800 - 1.20 µm/m-°C @Temperature 23.0 - 55.0 °C | 0.444 - 0.667 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1/-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 57.0 °C | 135 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 68.0 °C @Load 5.10 kg | 154 °F @Load 11.2 lb | ISO 306 | ||
| Decomposition Temperature | >= 300 °C | >= 572 °F | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| V-2 @Thickness 3.20 mm | V-2 @Thickness 0.126 in | ||||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 30.0 °C | 86.0 °F | Hopper Throat | ||
| Zone 1 | 200 °C | 392 °F | Feed Zone | ||
| Zone 2 | 240 °C | 464 °F | Compression | ||
| Zone 3 | 240 °C | 464 °F | Metering-zone | ||
| Zone 4 | 240 °C | 464 °F | Nozzle | ||
| Melt Temperature | 240 °C | 464 °F | Optimal | ||
| 230 - 260 °C | 446 - 500 °F | Injection-molding/Extrusion | |||
| Mold Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | Injection-molding | ||
| 40.0 °C | 104 °F | Optimal | |||
| Drying Temperature | 60.0 °C | 140 °F | |||
| Dry Time | 8 hour | 8 hour | |||
| Moisture Content | 0.030 - 0.060 % | 0.030 - 0.060 % | Optimal | ||
| <= 0.15 % | <= 0.15 % | ||||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >400°C | ASTM D1929 | |||
| Peripheral Screw Speed | < 0.3 m/s | ||||