- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 5.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 | ||
| Water Absorption | 5.5 % | 5.5 % | ISO 62 | ||
| Moisture Absorption | 2.00 % | 2.00 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 105 MPa | 15200 psi | conditioned; ISO 2039-1 | ||
| 210 MPa | 30500 psi | dry; ISO 2039-1 | |||
| Tensile Strength at Break | 90.0 MPa | 13100 psi | conditioned; ISO 527-1/-2 | ||
| 155 MPa | 22500 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | 3.0 % | 3.0 % | dry; ISO 527-1/-2 | ||
| 6.0 % | 6.0 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 5.50 GPa | 798 ksi | conditioned; ISO 527-1/-2 | ||
| 9.50 GPa | 1380 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | dry; ISO 179/1eU | ||
| 7.00 J/cm² | 33.3 ft-lb/in² | conditioned; ISO 179/1eU | |||
| 6.50 J/cm² @Temperature 30.0 °C | 30.9 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 6.50 J/cm² @Temperature 30.0 °C | 30.9 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | dry; ISO 179/1eA | ||
| 1.10 J/cm² | 5.23 ft-lb/in² | conditioned; ISO 179/1eA | |||
| 0.700 J/cm² @Temperature 30.0 °C | 3.33 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 0.700 J/cm² @Temperature 30.0 °C | 3.33 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | conditioned; IEC 60093 | ||
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | dry; IEC 60093 | |||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | conditioned; IEC 60243-1 | ||
| 38.0 kV/mm | 965 kV/in | dry; IEC 60243-1 | |||
| Comparative Tracking Index | 500 V | 500 V | conditioned; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 130 - 150 °C | 266 - 302 °F | long term; EMS | ||
| 230 °C | 446 °F | short term; EMS | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 155 °C | 311 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Automotive | Air intake sytems | ||||
| Form | Granules | ||||
| Processing | Extrusion - blow molding | ||||
| Injection Molding | |||||
| Other Extrusion | |||||
| Product Attributes | Nanocomposite | ||||
| Special Characteristics | Improved heat resistance | ||||