- 密度 [g/cm3]: 1.09
- 缺口冲击强度: 8.0
- 拉伸强度 [MPa]: 35.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ISO 1183/A |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 72 | 72 | Conditioned; ISO 868 |
| 78 | 78 | ISO 868 | |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | Conditioned; ISO R 527 |
| 55.0 MPa | 7980 psi | ISO R 527 | |
| Elongation at Yield | 50 % | 50 % | ISO R 527 |
| >= 50 % | >= 50 % | Conditioned; ISO R 527 | |
| Modulus of Elasticity | 0.600 GPa | 87.0 ksi | Conditioned; ISO 178 |
| 1.90 GPa | 276 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180/1A |
| 20.0 kJ/m² | 9.52 ft-lb/in² | Conditioned; ISO 180/1A | |
| Charpy Impact Unnotched | NB | NB | ISO 179/IeU |
| NB | NB | Conditioned; ISO 179/IeU | |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179/IeA |
| NB | NB | Conditioned; ISO 179/IeA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | Conditioned; CEI 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | CEI 60093 | |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | Conditioned; CEI 60093 |
| 1.00e+15 ohm | 1.00e+15 ohm | CEI 60093 | |
| Comparative Tracking Index | 600 V | 600 V | CEI 60112/Solution A |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 80.0 µm/m-°C | 44.4 µin/in-°F | ASTM E831 |
| Melting Point | 243 °C | 469 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75-2/AF |