- 密度 [g/cm3]: 1.12
- 吸水率 [%]: 8.5
- 拉伸强度 [MPa]: 35.0
- 热变形温度 [℃]: 160.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 | ||
| Water Absorption | 8.5 % | 8.5 % | ISO 62 | ||
| Moisture Absorption | 2.50 % | 2.50 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.012 cm/cm | 0.012 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 45.0 MPa | 6530 psi | conditioned; ISO 2039-1 | ||
| 125 MPa | 18100 psi | dry; ISO 2039-1 | |||
| Tensile Strength at Break | 40.0 MPa | 5800 psi | dry; ISO 527-1/-2 | ||
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | dry; ISO 527-1/-2 | ||
| 65.0 MPa | 9430 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | 25 % | 25 % | dry; ISO 527-1/-2 | ||
| 25 % | 25 % | dry; ISO 527-1/-2 | |||
| >= 50 % | >= 50 % | conditioned; ISO 527-1/-2 | |||
| Elongation at Yield | 4.0 % | 4.0 % | dry; ISO 527-1/-2 | ||
| 20 % | 20 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 0.750 GPa | 109 ksi | conditioned; ISO 527-1/-2 | ||
| 2.40 GPa | 348 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | NB | NB | dry; ISO 179/1eU | ||
| NB | NB | conditioned; ISO 179/1eU | |||
| NB @Temperature 30.0 °C | NB @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| NB @Temperature 30.0 °C | NB @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | dry; ISO 179/1eA | ||
| 4.50 J/cm² | 21.4 ft-lb/in² | conditioned; ISO 179/1eA | |||
| 0.800 J/cm² @Temperature 30.0 °C | 3.81 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| 1.00 J/cm² @Temperature 30.0 °C | 4.76 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | conditioned; IEC 60093 | ||
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | dry; IEC 60093 | |||
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | IEC 60093 | ||
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | conditioned; IEC 60243-1 | ||
| 31.0 kV/mm | 787 kV/in | dry; IEC 60243-1 | |||
| Comparative Tracking Index | 600 V | 600 V | conditioned; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 150 µm/m-°C | 83.3 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 100 - 120 °C | 212 - 248 °F | long term; EMS | ||
| 180 °C | 356 °F | short term; EMS | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Automotive | Automotive electr. and electronics, lighting | ||||
| Electricals & Electronics | Connectors | ||||
| Form | Granules | ||||
| Industry & Consumer goods | Mechanical Engineering | ||||
| Power transmission | |||||
| Sports & Leisure | |||||
| Tools & Accessories | |||||
| Processing | Injection Molding | ||||
| Special Characteristics | High impact or impact modified | ||||