- 密度 [g/cm3]: 1.46
- 吸水率 [%]: 5.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 | ||
| Water Absorption | 5.0 % | 5.0 % | ISO 62 | ||
| Moisture Absorption | 2.00 % | 2.00 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | conditioned; ISO 527-1/-2 | ||
| 100 MPa | 14500 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | 4.0 % | 4.0 % | dry; ISO 527-1/-2 | ||
| 8.0 % | 8.0 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 3.00 GPa | 435 ksi | conditioned; ISO 527-1/-2 | ||
| 6.50 GPa | 943 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | dry; ISO 179/1eU | ||
| 5.00 J/cm² | 23.8 ft-lb/in² | conditioned; ISO 179/1eU | |||
| 3.00 J/cm² @Temperature 30.0 °C | 14.3 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 3.00 J/cm² @Temperature 30.0 °C | 14.3 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | dry; ISO 179/1eA | ||
| 0.800 J/cm² | 3.81 ft-lb/in² | conditioned; ISO 179/1eA | |||
| 0.300 J/cm² @Temperature 30.0 °C | 1.43 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 0.300 J/cm² @Temperature 30.0 °C | 1.43 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 90.0 - 110 °C | 194 - 230 °F | long term; EMS | ||
| 180 °C | 356 °F | short term; EMS | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 70.0 °C | 158 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Automotive | Automotive electr. and electronics, lighting | ||||
| Interior | |||||
| Powertrain and Chassis | |||||
| Form | Granules | ||||
| Industry & Consumer goods | Mechanical Engineering | ||||
| Power transmission | |||||
| Sports & Leisure | |||||
| Tools & Accessories | |||||
| Processing | Injection Molding | ||||
| Product Attributes | Improved friction & wear properties | ||||