- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 6.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 | ||
| Water Absorption | 6.5 % | 6.5 % | ISO 62 | ||
| Moisture Absorption | 2.00 % | 2.00 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 90.0 MPa | 13100 psi | conditioned; ISO 2039-1 | ||
| 170 MPa | 24700 psi | dry; ISO 2039-1 | |||
| Tensile Strength at Break | 45.0 MPa | 6530 psi | conditioned; ISO 527-1/-2 | ||
| 75.0 MPa | 10900 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | 3.0 % | 3.0 % | dry; ISO 527-1/-2 | ||
| 15 % | 15 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 2.30 GPa | 334 ksi | conditioned; ISO 527-1/-2 | ||
| 5.80 GPa | 841 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | dry; ISO 179/1eU | ||
| 12.0 J/cm² | 57.1 ft-lb/in² | conditioned; ISO 179/1eU | |||
| 3.50 J/cm² @Temperature 30.0 °C | 16.7 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 3.50 J/cm² @Temperature 30.0 °C | 16.7 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | dry; ISO 179/1eA | ||
| 0.700 J/cm² | 3.33 ft-lb/in² | conditioned; ISO 179/1eA | |||
| 0.300 J/cm² @Temperature 30.0 °C | 1.43 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| 0.500 J/cm² @Temperature 30.0 °C | 2.38 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | conditioned; IEC 60093 | ||
| 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | dry; IEC 60093 | |||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | dry; IEC 60243-1 | ||
| 27.0 kV/mm | 686 kV/in | conditioned; IEC 60243-1 | |||
| Comparative Tracking Index | 525 V | 525 V | conditioned; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 100 - 120 °C | 212 - 248 °F | long term; EMS | ||
| 220 °C | 428 °F | short term; EMS | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 70.0 °C | 158 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Form | Granules | ||||
| Processing | Injection Molding | ||||