- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 7.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 | ||
| Water Absorption | 7.0 % | 7.0 % | ISO 62 | ||
| Moisture Absorption | 2.00 % | 2.00 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 120 MPa | 17400 psi | conditioned; ISO 2039-1 | ||
| 175 MPa | 25400 psi | dry; ISO 2039-1 | |||
| Tensile Strength at Break | 45.0 MPa | 6530 psi | conditioned; ISO 527-1/-2 | ||
| 90.0 MPa | 13100 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | 2.0 % | 2.0 % | dry; ISO 527-1/-2 | ||
| 9.0 % | 9.0 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 3.70 GPa | 537 ksi | conditioned; ISO 527-1/-2 | ||
| 8.50 GPa | 1230 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | dry; ISO 179/1eU | ||
| 6.00 J/cm² | 28.6 ft-lb/in² | conditioned; ISO 179/1eU | |||
| 3.00 J/cm² @Temperature 30.0 °C | 14.3 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 3.00 J/cm² @Temperature 30.0 °C | 14.3 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | dry; ISO 179/1eA | ||
| 0.600 J/cm² | 2.86 ft-lb/in² | conditioned; ISO 179/1eA | |||
| 0.300 J/cm² @Temperature 30.0 °C | 1.43 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 0.300 J/cm² @Temperature 30.0 °C | 1.43 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | conditioned; IEC 60093 | ||
| 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | dry; IEC 60093 | |||
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | IEC 60093 | ||
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | conditioned; IEC 60243-1 | ||
| 34.0 kV/mm | 864 kV/in | dry; IEC 60243-1 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 80.0 - 110 °C | 176 - 230 °F | long term; EMS | ||
| 160 °C | 320 °F | short term; EMS | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 155 °C | 311 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 65.0 °C | 149 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Automotive | Exterior | ||||
| Form | Granules | ||||
| Industry & Consumer goods | Mechanical Engineering | ||||
| Sports & Leisure | |||||
| Processing | Injection Molding | ||||
| Special Characteristics | Improved UV resistance (outdoor use) | ||||
| Light stabilized or stable to light | |||||