- 密度 [g/cm3]: 1.33
- 吸水率 [%]: 6.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 | ||
| Water Absorption | 6.0 % | 6.0 % | ISO 62 | ||
| Moisture Absorption | 2.00 % | 2.00 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.014 cm/cm | 0.014 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 135 MPa | 19600 psi | conditioned; ISO 2039-1 | ||
| 180 MPa | 26100 psi | dry; ISO 2039-1 | |||
| Tensile Strength at Break | 50.0 MPa | 7250 psi | conditioned; ISO 527-1/-2 | ||
| 85.0 MPa | 12300 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | 7.0 % | 7.0 % | dry; ISO 527-1/-2 | ||
| 35 % | 35 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 2.10 GPa | 305 ksi | conditioned; ISO 527-1/-2 | ||
| 4.80 GPa | 696 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature 30.0 °C | 19.0 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | ||
| 5.00 J/cm² @Temperature 30.0 °C | 23.8 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | dry; ISO 179/1eA | ||
| 0.500 J/cm² | 2.38 ft-lb/in² | conditioned; ISO 179/1eA | |||
| 0.300 J/cm² @Temperature 30.0 °C | 1.43 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 0.400 J/cm² @Temperature 30.0 °C | 1.90 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | conditioned; IEC 60093 | ||
| 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | dry; IEC 60093 | |||
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 90.0 - 120 °C | 194 - 248 °F | long term; EMS | ||
| 180 °C | 356 °F | short term; EMS | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Form | Granules | ||||
| Processing | Injection Molding | ||||