- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 5.0
- 拉伸强度 [MPa]: 50.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 | ||
| Water Absorption | 5.0 % | 5.0 % | ISO 62 | ||
| Moisture Absorption | 2.00 % | 2.00 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm | 0.0090 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 65.0 MPa | 9430 psi | conditioned; ISO 2039-1 | ||
| 140 MPa | 20300 psi | dry; ISO 2039-1 | |||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | dry; ISO 527-1/-2 | ||
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | conditioned; ISO 527-1/-2 | ||
| 90.0 MPa | 13100 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | 12 % | 12 % | dry; ISO 527-1/-2 | ||
| 12 % | 12 % | dry; ISO 527-1/-2 | |||
| >= 50 % | >= 50 % | conditioned; ISO 527-1/-2 | |||
| Elongation at Yield | 5.0 % | 5.0 % | dry; ISO 527-1/-2 | ||
| 15 % | 15 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 1.40 GPa | 203 ksi | conditioned; ISO 527-1/-2 | ||
| 3.30 GPa | 479 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | NB | NB | dry; ISO 179/1eU | ||
| NB | NB | conditioned; ISO 179/1eU | |||
| NB @Temperature 30.0 °C | NB @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| NB @Temperature 30.0 °C | NB @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | dry; ISO 179/1eA | ||
| 0.800 J/cm² | 3.81 ft-lb/in² | conditioned; ISO 179/1eA | |||
| 0.400 J/cm² @Temperature 30.0 °C | 1.90 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 0.400 J/cm² @Temperature 30.0 °C | 1.90 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | conditioned; IEC 60093 | ||
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | dry; IEC 60093 | |||
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | IEC 60093 | ||
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | conditioned; IEC 60243-1 | ||
| 27.0 kV/mm | 686 kV/in | dry; IEC 60243-1 | |||
| Comparative Tracking Index | 475 V | 475 V | conditioned; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 80.0 - 100 °C | 176 - 212 °F | long term; EMS | ||
| 200 °C | 392 °F | short term; EMS | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 65.0 °C | 149 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Automotive | Interior | ||||
| Powertrain and Chassis | |||||
| Form | Granules | ||||
| Industry & Consumer goods | Mechanical Engineering | ||||
| Power transmission | |||||
| Tools & Accessories | |||||
| Processing | Injection Molding | ||||
| Product Attributes | Improved friction & wear properties | ||||