- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.27
- 弯曲模量 [MPa]: 18.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | |
| Viscosity Measurement | 0.89 - 1.04 | 0.89 - 1.04 | |
| Linear Mold Shrinkage | 0.0089 cm/cm | 0.0089 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0104 cm/cm | 0.0104 in/in | |
| Melt Flow | 1.0 g/10 min @Load 0.325 kg, Temperature 270 °C | 1.0 g/10 min @Load 0.716 lb, Temperature 518 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 220 MPa | 31900 psi | |
| Elongation at Break | 2.0 % | 2.0 % | |
| Tensile Modulus | 19.5 GPa | 2830 ksi | |
| Flexural Strength | 330 MPa | 47900 psi | |
| Flexural Modulus | 18.0 GPa | 2610 ksi | |
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature 23.0 °C | 21.4 ft-lb/in² @Temperature 73.4 °F | |
| 5.00 J/cm² @Temperature -20.0 °C | 23.8 ft-lb/in² @Temperature -4.00 °F | ||
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -20.0 °C | 1.90 ft-lb/in² @Temperature -4.00 °F | |
| 0.700 J/cm² @Temperature 23.0 °C | 3.33 ft-lb/in² @Temperature 73.4 °F | ||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 - 260 °C | 428 - 500 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | |
| Vicat Softening Point | 205 °C | 401 °F | B |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.10 % | 0.10 % | |
| Injection Pressure | 100 - 150 MPa | 14500 - 21800 psi | |