- 密度 [g/cm3]: 1.36
- 弯曲模量 [MPa]: 8.80
- 热变形温度 [℃]: 250.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Filler Content | 30 % | 30 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | With Flow; ISO 2577 |
| 0.011 cm/cm | 0.011 in/in | Across Flow; ISO 2577 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | <= 175 MPa | <= 25400 psi | ISO/R527 |
| Elongation at Yield | 5.0 % | 5.0 % | ISO/R527 |
| Flexural Strength | <= 243 MPa | <= 35200 psi | ISO 178 |
| Flexural Modulus | 8.80 GPa @Temperature 23.0 °C | 1280 ksi @Temperature 73.4 °F | ISO 178 |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature -20.0 °C | 19.0 ft-lb/in² @Temperature -4.00 °F | ISO 179 |
| 4.20 J/cm² @Temperature 23.0 °C | 20.0 ft-lb/in² @Temperature 73.4 °F | ISO 179 | |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -20.0 °C | 2.86 ft-lb/in² @Temperature -4.00 °F | ISO 179 |
| 0.800 J/cm² @Temperature 23.0 °C | 3.81 ft-lb/in² @Temperature 73.4 °F | ISO 179 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | >= 230 °C @Load 5.001 kg | >= 446 °F @Load 11.03 lb | 50°C/h; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| Glow Wire Test | 650 °C @Thickness 2.00 mm | 1200 °F @Thickness 0.0787 in | IEC 695-2-1 |