- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.58
- 弯曲模量 [MPa]: 12.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | |
| Viscosity Measurement | 0.40 - 0.88 | 0.40 - 0.88 | |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0088 cm/cm | 0.0088 in/in | |
| Melt Flow | 2.0 g/10 min @Load 0.325 kg, Temperature 270 °C | 2.0 g/10 min @Load 0.716 lb, Temperature 518 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 210 MPa | 30500 psi | |
| Elongation at Break | 2.0 % | 2.0 % | |
| Tensile Modulus | 14.5 GPa | 2100 ksi | |
| Flexural Strength | 290 MPa | 42100 psi | |
| Flexural Modulus | 12.5 GPa | 1810 ksi | |
| Charpy Impact Unnotched | 8.50 J/cm² @Temperature -20.0 °C | 40.4 ft-lb/in² @Temperature -4.00 °F | |
| 10.5 J/cm² @Temperature 23.0 °C | 50.0 ft-lb/in² @Temperature 73.4 °F | ||
| Charpy Impact, Notched | 1.70 J/cm² @Temperature -20.0 °C | 8.09 ft-lb/in² @Temperature -4.00 °F | |
| 2.10 J/cm² @Temperature 23.0 °C | 9.99 ft-lb/in² @Temperature 73.4 °F | ||
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 5.00e+11 ohm-cm | 5.00e+11 ohm-cm | |
| Surface Resistance | 8.00e+13 ohm | 8.00e+13 ohm | |
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | |
| Comparative Tracking Index | 55 V | 55 V | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 238 °C | 460 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | |
| Vicat Softening Point | 235 °C | 455 °F | B |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |
| Mold Temperature | 90.0 - 100 °C | 194 - 212 °F | |
| Drying Temperature | 90.0 °C | 194 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.15 % | 0.15 % | |
| Injection Pressure | 90.0 - 150 MPa | 13100 - 21800 psi | |