- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.09
- 弯曲模量 [MPa]: 2.02
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | |
| Viscosity Measurement | 2.8 - 3.5 | 2.8 - 3.5 | |
| Linear Mold Shrinkage | 0.035 cm/cm | 0.035 in/in | |
| Linear Mold Shrinkage, Transverse | 0.028 cm/cm | 0.028 in/in | |
| Melt Flow | 2.0 g/10 min @Load 0.325 kg, Temperature 270 °C | 2.0 g/10 min @Load 0.716 lb, Temperature 518 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 55.0 MPa | 7980 psi | |
| Elongation at Break | 24 % | 24 % | |
| Tensile Modulus | 2.15 GPa | 312 ksi | |
| Flexural Strength | 70.0 MPa | 10200 psi | |
| Flexural Modulus | 2.02 GPa | 293 ksi | |
| Charpy Impact Unnotched | NB @Temperature -20.0 °C | NB @Temperature -4.00 °F | |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ||
| Charpy Impact, Notched | 0.900 J/cm² @Temperature -20.0 °C | 4.28 ft-lb/in² @Temperature -4.00 °F | |
| 4.20 J/cm² @Temperature 23.0 °C | 20.0 ft-lb/in² @Temperature 73.4 °F | ||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | |
| Vicat Softening Point | 190 °C | 374 °F | B |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.15 % | 0.15 % | |
| Injection Pressure | 70.0 - 120 MPa | 10200 - 17400 psi | |