- 缺口冲击强度: 85.0
- 拉伸强度 [MPa]: 28.0
- 断裂伸长率 [%]: 7.00
- 弯曲模量 [MPa]: 0.230
- 热变形温度 [℃]: 53.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.027 g/cc | 1.027 g/cc | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ISO 527-1,-2 | ||
| Elongation at Yield | 6.5 % | 6.5 % | ISO 527-1,-2 | ||
| Tensile Modulus | 0.210 GPa | 30.5 ksi | Conditioned; ISO 527-1,-2 | ||
| 0.980 GPa | 142 ksi | ISO 527-1,-2 | |||
| Flexural Strength | 12.0 MPa @Strain 9.00 % | 1740 psi @Strain 9.00 % | Conditioned; ISO 178 | ||
| 35.0 MPa @Strain 6.10 % | 5080 psi @Strain 6.10 % | ISO 178 | |||
| Flexural Yield Strength | 7.00 MPa @Strain 3.50 % | 1020 psi @Strain 3.50 % | Conditioned; ISO 178 | ||
| 30.0 MPa @Strain 3.50 % | 4350 psi @Strain 3.50 % | ISO 178 | |||
| Flexural Modulus | 0.230 GPa | 33.4 ksi | Conditioned; ISO 178 | ||
| 0.980 GPa | 142 ksi | ISO 178 | |||
| Izod Impact, Notched (ISO) | 85.0 kJ/m² @Temperature -30.0 °C | 40.4 ft-lb/in² @Temperature -22.0 °F | ISO 180-1A | ||
| 90.0 kJ/m² @Temperature 23.0 °C | 42.8 ft-lb/in² @Temperature 73.4 °F | ISO 180-1A | |||
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180-1U | ||
| Charpy Impact, Notched | 10.5 J/cm² @Temperature -30.0 °C | 50.0 ft-lb/in² @Temperature -22.0 °F | ISO 179-1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 200 µm/m-°C | 111 µin/in-°F | ISO 11359-1,-2 | ||
| CTE, linear, Transverse to Flow | 200 µm/m-°C | 111 µin/in-°F | ISO 11359-1,-2 | ||
| Melting Point | 211 °C | 412 °F | ISO 11357-1,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 53.0 °C | 127 °F | ISO 75-1,-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.0 °C | 118 °F | ISO 75-1,-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 230 - 280 °C | 446 - 536 °F | Recommended | ||
| 270 °C | 518 °F | Processing conditions for test specimens; ISO 294 | |||
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Recommended | ||
| 80.0 °C | 176 °F | Processing conditions for test specimens; ISO 294 | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 2 - 6 hour | 2 - 6 hour | |||
| Moisture Content | 0.00 - 0.060 % | 0.00 - 0.060 % | Residual; Acc. To Karl Fischer | ||
| Descriptive Properties | |||||
| ISO Shortname | ISO 1874-PA 6/66-HI,BHS,14-010 | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.