- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.32
- 弯曲模量 [MPa]: 6.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | |
| Viscosity Measurement | 0.19 - 0.79 | 0.19 - 0.79 | |
| Linear Mold Shrinkage | 0.0079 cm/cm | 0.0079 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0019 cm/cm | 0.0019 in/in | |
| Melt Flow | 3.0 g/10 min @Load 0.325 kg, Temperature 270 °C | 3.0 g/10 min @Load 0.716 lb, Temperature 518 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 135 MPa | 19600 psi | |
| Elongation at Break | 3.0 % | 3.0 % | |
| Tensile Modulus | 7.00 GPa | 1020 ksi | |
| Flexural Strength | 200 MPa | 29000 psi | |
| Flexural Modulus | 6.00 GPa | 870 ksi | |
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature -20.0 °C | 21.4 ft-lb/in² @Temperature -4.00 °F | |
| 5.00 J/cm² @Temperature 23.0 °C | 23.8 ft-lb/in² @Temperature 73.4 °F | ||
| Charpy Impact, Notched | 0.800 J/cm² @Temperature -20.0 °C | 3.81 ft-lb/in² @Temperature -4.00 °F | |
| 0.900 J/cm² @Temperature 23.0 °C | 4.28 ft-lb/in² @Temperature 73.4 °F | ||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | |
| Vicat Softening Point | 250 °C | 482 °F | B |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.15 % | 0.15 % | |
| Injection Pressure | 70.0 - 120 MPa | 10200 - 17400 psi | |