- 密度 [g/cm3]: 1.49
- 缺口冲击强度: 3.0
- 拉伸强度 [MPa]: 75.0
- 弯曲模量 [MPa]: 6.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183/A | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | ISO R 527 | ||
| Elongation at Break | 2.0 % | 2.0 % | ISO R 527 | ||
| Tensile Modulus | 10.4 GPa | 1510 ksi | ISO R 527 | ||
| Flexural Strength | 110 MPa | 16000 psi | at break; ISO 178 | ||
| Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | ISO 180/1eA | ||
| Charpy Impact Unnotched | 1.60 J/cm² | 7.61 ft-lb/in² | ISO 179/1eU | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 245 °C | 473 °F | |||
| Glow Wire Test | 960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | CEI 695 | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |||
| Nozzle Temperature | 250 - 270 °C | 482 - 518 °F | |||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| Descriptive Properties | |||||
| Compression Zone | 260-280°C | ||||
| Mixing Zone | 250-270°C | ||||