- 密度 [g/cm3]: 1.07
- 吸水率 [%]: 1.15
- 缺口冲击强度: 85.0
- 拉伸强度 [MPa]: 35.0
- 弯曲模量 [MPa]: 0.850
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183/A | ||
| Water Absorption | 1.15 % @Temperature 23.0 °C, Time 86400 sec | 1.15 % @Temperature 73.4 °F, Time 24.0 hour | ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | ISO 527 type 1 A | ||
| Elongation at Break | 220 % | 220 % | ISO 527 Type 1A | ||
| Tensile Modulus | 0.900 GPa | 131 ksi | ISO 527 Type 1A | ||
| Flexural Strength | 40.0 MPa | 5800 psi | ISO 178 | ||
| Flexural Modulus | 0.850 GPa | 123 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 85.0 kJ/m² | 40.4 ft-lb/in² | ISO 180/1eA | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| Charpy Impact, Notched | NB | NB | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Dielectric Constant | 3.7 | 3.7 | IEC 60250 | ||
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature 23.0 - 85.0 °C | 38.9 µin/in-°F @Temperature 73.4 - 185 °F | ISO 11359 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75/Af | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 200 - 210 °C | 392 - 410 °F | |||
| Front Barrel Temperature | 210 - 220 °C | 410 - 428 °F | |||
| Die Temperature | 220 - 230 °C | 428 - 446 °F | |||
| Melt Temperature | 222 °C | 432 °F | ISO 11357 | ||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| Descriptive Properties | |||||
| Compression Zone | 210-220°C | ||||