- 吸水率 [%]: 1.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Water Absorption | 1.1 % @Temperature 23.0 °C, Time 86400 sec | 1.1 % @Temperature 73.4 °F, Time 24.0 hour | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0075 cm/cm | 0.0075 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.0112 cm/cm | 0.0112 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527 Type 1A | ||
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 Type 1A | ||
| Tensile Modulus | 6.13 GPa | 889 ksi | ISO 527 Type 1A | ||
| Izod Impact, Unnotched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | ISO 180/1eU | ||
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Flammability, UL94 | V-2 @Thickness 0.800 mm | V-2 @Thickness 0.0315 in | 1210 | ||
| V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | 1210 | |||
| V-2 @Thickness 3.20 mm | V-2 @Thickness 0.126 in | 1210 | |||
| Glow Wire Test | 700 °C @Thickness 0.800 mm | 1290 °F @Thickness 0.0315 in | ignition temperature; ISO 60695-2-13 | ||
| 725 °C @Thickness 1.60 mm | 1340 °F @Thickness 0.0630 in | ignition temperature; ISO 60695-2-13 | |||
| 960 °C @Thickness 0.800 mm | 1760 °F @Thickness 0.0315 in | ISO 60695-2-12 | |||
| 960 °C @Thickness 1.60 mm | 1760 °F @Thickness 0.0630 in | ISO 60695-2-12 | |||
| 960 °C @Thickness 3.20 mm | 1760 °F @Thickness 0.126 in | ISO 60695-2-12 | |||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 220 - 230 °C | 428 - 446 °F | |||
| Front Barrel Temperature | 245 - 255 °C | 473 - 491 °F | |||
| Melt Temperature | 220 °C | 428 °F | ISO 11357 | ||
| Mold Temperature | 80.0 °C | 176 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| Descriptive Properties | |||||
| Compression Zone | 230-240°C | ||||