- 密度 [g/cm3]: 1.16
- 缺口冲击强度: 15.0
- 拉伸强度 [MPa]: 50.0
- 弯曲模量 [MPa]: 2.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183/A |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | ISO 527 Type 1A |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527 type 1 A |
| Elongation at Break | 38 % | 38 % | ISO 527 Type 1A |
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527 type 1 A |
| Tensile Modulus | 2.00 GPa | 290 ksi | ISO 527 Type 1A |
| Flexural Strength | 70.0 MPa | 10200 psi | ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO 180/1eA |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 3.9 | 3.9 | IEC 60250 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243 |
| Dissipation Factor | 0.060 | 0.060 | IEC 60250 |
| Comparative Tracking Index | 60 V | 60 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
| Moisture Content | <= 0.20 % | <= 0.20 % | |