- 熔体流动速率 [g/10min]: 3.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 | ||
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | at 190°C/2.16 kg; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 33 | 33 | ASTM D2240 | ||
| Tensile Strength at Break | 6.72 MPa | 975 psi | ASTM D412 | ||
| Elongation at Break | 900 % | 900 % | ASTM D412 | ||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 171 - 193 °C | 340 - 380 °F | |||
| Middle Barrel Temperature | 177 - 199 °C | 350 - 390 °F | |||
| Front Barrel Temperature | 182 - 204 °C | 360 - 400 °F | |||
| Nozzle Temperature | 188 - 210 °C | 370 - 410 °F | |||
| Zone 1 | 166 - 188 °C | 330 - 370 °F | |||
| Zone 2 | 171 - 193 °C | 340 - 380 °F | |||
| Zone 3 | 177 - 199 °C | 350 - 390 °F | |||
| Zone 5 | 182 - 204 °C | 360 - 400 °F | |||
| Die Temperature | 190 - 210 °C | 374 - 410 °F | |||
| Melt Temperature | 188 - 210 °C | 370 - 410 °F | Processing Temperature | ||
| Mold Temperature | 25.0 - 65.6 °C | 77.0 - 150 °F | |||
| Injection Pressure | 1.38 - 6.89 MPa | 200 - 1000 psi | |||
| Back Pressure | 0.172 - 0.345 MPa | 25.0 - 50.0 psi | |||
| Cushion | 0.381 - 2.54 cm | 0.150 - 1.00 in | |||
| Screw Speed | 50 - 100 rpm | 50 - 100 rpm | |||
| Descriptive Properties | |||||
| Appearance | Opaque | ||||