- 密度 [g/cm3]: 1.19
- 吸水率 [%]: 0.7
- 缺口冲击强度: 1.33
- 拉伸强度 [MPa]: 65.5
- 弯曲模量 [MPa]: 1.45
- 硬度: 112.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Water Absorption | 0.70 % @Time 86400 sec | 0.70 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm @Thickness 3.17 mm | 0.0090 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 112 | 112 | ASTM D785 |
| Tensile Strength, Yield | 65.5 MPa | 9500 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm @Thickness 3.17 mm | 2.50 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | ASTM D257 |
| Dielectric Strength | 20.9 kV/mm | 530 kV/in | Method A (Short-Time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 59.4 µm/m-°C | 33.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 92.8 °C | 199 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |