TP Composites Plastiblend® PA6/6,6 109 L Nylon 6/66

TP Composites Plastiblend® PA6/6,6 109 L Nylon 6/66 物性表: TP Composites Plastiblend® PA6/6,6 109 L Nylon 6/66物性表及特性介绍,TP Composites Plastiblend® PA6/6,6 109 L Nylon 6/66注塑参数详情,如需TP Composites Plastiblend® PA6/6,6 109 L Nylon 6/66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.14
  • 吸水率 [%]: 1.5
  • 缺口冲击强度: 0.534
  • 断裂伸长率 [%]: 110
  • 弯曲模量 [MPa]: 2.83
  • 硬度: 119.0
  • 热变形温度 [℃]: 216.0
 
Physical PropertiesMetricEnglishComments
Density 1.14 g/cc0.0412 lb/in³ASTM D792
Water Absorption 1.5 %
@Time 86400 sec
1.5 %
@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.010 cm/cm
@Thickness 3.17 mm
0.010 in/in
@Thickness 0.125 in
ASTM D955
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell R 119119ASTM D785
Tensile Strength 93.1 MPa13500 psiASTM D638
Elongation at Yield 30 %30 %ASTM D638
Flexural Yield Strength 110 MPa16000 psiASTM D790
Flexural Modulus 2.83 GPa410 ksiASTM D790
Izod Impact, Notched 0.534 J/cm
@Thickness 3.17 mm
1.00 ft-lb/in
@Thickness 0.125 in
ASTM D256
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 1.00e+13 ohm-cm1.00e+13 ohm-cmASTM D257
Dielectric Strength 17.3 kV/mm440 kV/inMethod A (Short-Time); ASTM D149
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow 72.0 µm/m-°C40.0 µin/in-°FASTM D696
Melting Point 240 °C464 °F
Deflection Temperature at 0.46 MPa (66 psi) 216 °C420 °FUnannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C176 °FUnannealed; ASTM D648
Flammability, UL94 V-2
@Thickness 1.50 mm
V-2
@Thickness 0.0591 in

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-44513.html

免责声明: 本文 TP Composites Plastiblend® PA6/6,6 109 L Nylon 6/66 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4