| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Relative Viscosity | 3.8 cP | 3.8 cP | 96% H2SO4 | ||
| 4.1 cP | 4.1 cP | 98% H2SO4 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 540 % | 540 % | |||
| Film Elongation at Break, TD | 550 % | 550 % | |||
| Secant Modulus, MD | 0.210 GPa | 30.5 ksi | |||
| Secant Modulus, TD | 0.200 GPa | 29.0 ksi | |||
| Coefficient of Friction, Dynamic | 0.23 | 0.23 | |||
| Coefficient of Friction, Static | 0.32 | 0.32 | |||
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | |||
| Film Tensile Strength at Break, TD | 39.0 MPa | 5660 psi | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 187 - 197 °C | 369 - 387 °F | |||
| Optical Properties | Metric | English | Comments | ||
| Haze | 9.5 % | 9.5 % | |||
| Gloss | 124 % | 124 % | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 190 - 210 °C | 374 - 410 °F | C1 | ||
| 220 - 230 °C | 428 - 446 °F | C2 | |||
| 230 - 240 °C | 446 - 464 °F | C3 | |||
| 230 - 240 °C | 446 - 464 °F | C4 | |||
| 240 - 250 °C | 464 - 482 °F | AD | |||
| 240 - 250 °C | 464 - 482 °F | CF | |||
| 240 - 250 °C | 464 - 482 °F | D1- D4 | |||
| Descriptive Properties | |||||
| Degree of Curling | 0 Mm | ||||