- 密度 [g/cm3]: 1.18
- 缺口冲击强度: 8.5
- 弯曲模量 [MPa]: 3.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183-87 |
| Filler Content | 10 % | 10 % | |
| Linear Mold Shrinkage, Flow | 0.0085 - 0.0095 cm/cm | 0.0085 - 0.0095 in/in | ISO DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.0090 cm/cm | 0.0080 - 0.0090 in/in | ISO DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527-93 |
| Elongation at Break | 8.0 % | 8.0 % | ISO 527-93 |
| Flexural Strength | 110 MPa | 16000 psi | ISO 178-93 |
| Flexural Modulus | 3.30 GPa | 479 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 8.50 kJ/m² | 4.04 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75-93 |