- 密度 [g/cm3]: 1.39
- 缺口冲击强度: 8.0
- 弯曲模量 [MPa]: 9.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183-87 |
| Filler Content | 33 % | 33 % | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0050 cm/cm | 0.0010 - 0.0050 in/in | ISO DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.011 cm/cm | 0.0070 - 0.011 in/in | ISO DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527-93 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-93 |
| Flexural Strength | 220 MPa | 31900 psi | ISO 178-93 |
| Flexural Modulus | 9.30 GPa | 1350 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75-93 |