- 密度 [g/cm3]: 1.71
- 缺口冲击强度: 17.0
- 弯曲模量 [MPa]: 17.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.71 g/cc | 0.0618 lb/in³ | ISO 1183-87 |
| Filler Content | 60 % | 60 % | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ISO DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0090 cm/cm | 0.0050 - 0.0090 in/in | ISO DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 215 MPa | 31200 psi | ISO 527-93 |
| Elongation at Break | 2.2 % | 2.2 % | ISO 527-93 |
| Flexural Strength | 325 MPa | 47100 psi | ISO 178-93 |
| Flexural Modulus | 17.8 GPa | 2580 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75-93 |