- 密度 [g/cm3]: 1.1
- 吸水率 [%]: 0.1
- 缺口冲击强度: 0.32
- 拉伸强度 [MPa]: 45.0
- 断裂伸长率 [%]: 103
- 弯曲强度 [MPa]: 65.0
- 弯曲模量 [MPa]: 2.48
- 硬度: 90.0
- 热变形温度 [℃]: 200.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 - 2.06 g/cc | 0.0397 - 0.0744 lb/in³ | Average value: 1.23 g/cc Grade Count:37 |
| Water Absorption | 0.100 - 13.5 % | 0.100 - 13.5 % | Average value: 8.42 % Grade Count:18 |
| Moisture Absorption at Equilibrium | 2.60 - 3.70 % | 2.60 - 3.70 % | Average value: 3.32 % Grade Count:20 |
| Water Absorption at Saturation | 7.00 - 14.0 % | 7.00 - 14.0 % | Average value: 10.0 % Grade Count:4 |
| Viscosity Test | 175 - 220 cm³/g | 175 - 220 cm³/g | Average value: 187 cm³/g Grade Count:7 |
| Linear Mold Shrinkage | 0.00330 - 0.0200 cm/cm | 0.00330 - 0.0200 in/in | Average value: 0.0187 cm/cm Grade Count:21 |
| Linear Mold Shrinkage, Transverse | 0.0200 cm/cm | 0.0200 in/in | Average value: 0.0200 cm/cm Grade Count:7 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 92.0 - 97.0 | 92.0 - 97.0 | Average value: 93.7 Grade Count:3 |
| Hardness, Rockwell R | 90.0 - 100 | 90.0 - 100 | Average value: 95.0 Grade Count:4 |
| Ball Indentation Hardness | 165 - 200 MPa | 23900 - 29000 psi | Average value: 172 MPa Grade Count:3 |
| Tensile Strength, Ultimate | 65.0 - 197 MPa | 9430 - 28500 psi | Average value: 107 MPa Grade Count:5 |
| Tensile Strength, Yield | 45.0 - 106 MPa | 6530 - 15400 psi | Average value: 74.1 MPa Grade Count:30 |
| Elongation at Break | 2.00 - 280 % | 2.00 - 280 % | Average value: 45.4 % Grade Count:25 |
| Elongation at Yield | 5.00 - 55.0 % | 5.00 - 55.0 % | Average value: 27.7 % Grade Count:25 |
| Modulus of Elasticity | 0.600 - 12.1 GPa | 87.0 - 1750 ksi | Average value: 2.46 GPa Grade Count:32 |
| Flexural Yield Strength | 103 - 283 MPa | 15000 - 41000 psi | Average value: 140 MPa Grade Count:9 |
| Flexural Modulus | 2.48 - 11.4 GPa | 360 - 1650 ksi | Average value: 4.72 GPa Grade Count:9 |
| Compressive Yield Strength | 23.0 - 110 MPa | 3340 - 16000 psi | Average value: 66.5 MPa Grade Count:3 |
| Izod Impact, Notched | 0.320 - 0.801 J/cm | 0.600 - 1.50 ft-lb/in | Average value: 0.651 J/cm Grade Count:8 |
| 0.74746 - 0.74746 J/cm @Temperature -40.0 - -40.0 °C | 1.4003 - 1.4003 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.747 J/cm Grade Count:2 | |
| 0.74746 - 0.74746 J/cm @Thickness 3.17 - 3.17 mm | 1.4003 - 1.4003 ft-lb/in @Thickness 0.125 - 0.125 in | Average value: 0.747 J/cm Grade Count:2 | |
| Izod Impact, Unnotched | 4.27 - 5340 J/cm | 8.00 - 10000 ft-lb/in | Average value: 8.81 J/cm Grade Count:4 |
| Charpy Impact Unnotched | 10.0 J/cm² - NB | 47.6 ft-lb/in² - NB | Average value: 10.0 J/cm² Grade Count:22 |
| 10.0 J/cm² - NB @Temperature -30.0 - -30.0 °C | 47.6 ft-lb/in² - NB @Temperature -22.0 - -22.0 °F | Average value: 11.3 J/cm² Grade Count:20 | |
| Charpy Impact, Notched | 0.500 - 1000 J/cm² | 2.38 - 4760 ft-lb/in² | Average value: 3.48 J/cm² Grade Count:27 |
| 0.400 - 3.00 J/cm² @Temperature -30.0 - -30.0 °C | 1.90 - 14.3 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 1.34 J/cm² Grade Count:20 | |
| Coefficient of Friction | 0.200 - 0.600 | 0.200 - 0.600 | Average value: 0.388 Grade Count:3 |
| Tensile Creep Modulus, 1000 hours | 500 - 850 MPa | 72500 - 123000 psi | Average value: 570 MPa Grade Count:5 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1000 - 1.00e+15 ohm-cm | 1000 - 1.00e+15 ohm-cm | Average value: 2.18e+14 ohm-cm Grade Count:29 |
| Surface Resistance | 1.00e+6 - 1.00e+14 ohm | 1.00e+6 - 1.00e+14 ohm | Average value: 1.71e+13 ohm Grade Count:9 |
| Dielectric Constant | 3.20 - 22.0 | 3.20 - 22.0 | Average value: 6.65 Grade Count:11 |
| Dielectric Strength | 15.0 - 30.0 kV/mm | 381 - 762 kV/in | Average value: 20.9 kV/mm Grade Count:23 |
| Dissipation Factor | 0.000500 - 0.0870 | 0.000500 - 0.0870 | Average value: 0.0194 Grade Count:9 |
| Comparative Tracking Index | 325 - 600 V | 325 - 600 V | Average value: 438 V Grade Count:23 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 36.0 - 160 µm/m-°C | 20.0 - 88.9 µin/in-°F | Average value: 86.5 µm/m-°C Grade Count:23 |
| CTE, linear, Transverse to Flow | 90.0 - 180 µm/m-°C | 50.0 - 100 µin/in-°F | Average value: 112 µm/m-°C Grade Count:13 |
| Thermal Conductivity | 0.300 - 0.980 W/m-K | 2.08 - 6.80 BTU-in/hr-ft²-°F | Average value: 0.471 W/m-K Grade Count:4 |
| Melting Point | 290 - 295 °C | 554 - 563 °F | Average value: 295 °C Grade Count:30 |
| Maximum Service Temperature, Air | 130 - 280 °C | 266 - 536 °F | Average value: 166 °C Grade Count:4 |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 - 291 °C | 392 - 555 °F | Average value: 263 °C Grade Count:12 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 - 285 °C | 194 - 545 °F | Average value: 179 °C Grade Count:23 |
| Vicat Softening Point | 250 - 290 °C | 482 - 554 °F | Average value: 283 °C Grade Count:7 |
| Glass Transition Temp, Tg | 75.0 - 80.0 °C | 167 - 176 °F | Average value: 75.6 °C Grade Count:9 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:16 |
| Oxygen Index | 24.0 - 29.0 % | 24.0 - 29.0 % | Average value: 26.8 % Grade Count:5 |