- 密度 [g/cm3]: 1.17
- 吸水率 [%]: 0.9
- 缺口冲击强度: 0.481
- 拉伸强度 [MPa]: 20.7
- 断裂伸长率 [%]: 96.5
- 弯曲强度 [MPa]: 70.0
- 弯曲模量 [MPa]: 2.90
- 热变形温度 [℃]: 290.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 - 1.87 g/cc | 0.0423 - 0.0676 lb/in³ | Average value: 1.52 g/cc Grade Count:89 |
| Filler Content | 10.0 - 60.0 % | 10.0 - 60.0 % | Average value: 32.3 % Grade Count:11 |
| Water Absorption | 0.900 - 9.50 % | 0.900 - 9.50 % | Average value: 4.70 % Grade Count:39 |
| Moisture Absorption at Equilibrium | 1.10 - 3.10 % | 1.10 - 3.10 % | Average value: 1.89 % Grade Count:39 |
| Viscosity Test | 70.0 - 150 cm³/g | 70.0 - 150 cm³/g | Average value: 123 cm³/g Grade Count:16 |
| Linear Mold Shrinkage | 0.00200 - 0.0150 cm/cm | 0.00200 - 0.0150 in/in | Average value: 0.00624 cm/cm Grade Count:61 |
| Linear Mold Shrinkage, Transverse | 0.00700 - 0.0150 cm/cm | 0.00700 - 0.0150 in/in | Average value: 0.0108 cm/cm Grade Count:19 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 70.0 - 255 MPa | 10200 - 37000 psi | Average value: 163 MPa Grade Count:72 |
| Tensile Strength, Yield | 20.7 - 231 MPa | 3000 - 33500 psi | Average value: 131 MPa Grade Count:14 |
| Elongation at Break | 1.30 - 10.0 % | 1.30 - 10.0 % | Average value: 4.09 % Grade Count:81 |
| Elongation at Yield | 2.10 - 7.50 % | 2.10 - 7.50 % | Average value: 4.09 % Grade Count:5 |
| Modulus of Elasticity | 2.80 - 20.7 GPa | 406 - 3000 ksi | Average value: 10.3 GPa Grade Count:68 |
| Flexural Yield Strength | 96.5 - 392 MPa | 14000 - 56800 psi | Average value: 238 MPa Grade Count:27 |
| Flexural Modulus | 2.90 - 19.3 GPa | 420 - 2800 ksi | Average value: 8.11 GPa Grade Count:31 |
| Izod Impact, Notched | 0.481 - 1.92 J/cm | 0.900 - 3.60 ft-lb/in | Average value: 1.04 J/cm Grade Count:25 |
| Izod Impact, Unnotched | 4.81 - 11.7 J/cm | 9.00 - 22.0 ft-lb/in | Average value: 8.25 J/cm Grade Count:11 |
| Izod Impact, Notched (ISO) | 9.00 - 20.0 kJ/m² | 4.28 - 9.52 ft-lb/in² | Average value: 14.7 kJ/m² Grade Count:3 |
| 8.00 - 15.0 kJ/m² @Temperature -40.0 - -40.0 °C | 3.81 - 7.14 ft-lb/in² @Temperature -40.0 - -40.0 °F | Average value: 10.3 kJ/m² Grade Count:3 | |
| Charpy Impact Unnotched | 2.50 - 10.0 J/cm² | 11.9 - 47.6 ft-lb/in² | Average value: 7.69 J/cm² Grade Count:39 |
| 5.00 - 8.00 J/cm² @Temperature -30.0 - -30.0 °C | 23.8 - 38.1 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 6.74 J/cm² Grade Count:34 | |
| Charpy Impact, Notched | 0.400 - 2.40 J/cm² | 1.90 - 11.4 ft-lb/in² | Average value: 1.37 J/cm² Grade Count:53 |
| 0.800 - 1.90 J/cm² @Temperature -30.0 - -30.0 °C | 3.81 - 9.04 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 1.17 J/cm² Grade Count:44 | |
| Tensile Creep Modulus, 1000 hours | 4500 - 12000 MPa | 653000 - 1.74e+6 psi | Average value: 7400 MPa Grade Count:10 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 10000 - 8.00e+15 ohm-cm | 10000 - 8.00e+15 ohm-cm | Average value: 4.36e+14 ohm-cm Grade Count:50 |
| Surface Resistance | 1.00e+12 - 1.00e+14 ohm | 1.00e+12 - 1.00e+14 ohm | Average value: 4.68e+13 ohm Grade Count:12 |
| Dielectric Constant | 4.00 - 16.0 | 4.00 - 16.0 | Average value: 6.52 Grade Count:17 |
| Dielectric Strength | 20.0 - 35.0 kV/mm | 508 - 889 kV/in | Average value: 25.4 kV/mm Grade Count:35 |
| Dissipation Factor | 0.000600 - 0.0700 | 0.000600 - 0.0700 | Average value: 0.0134 Grade Count:17 |
| Comparative Tracking Index | 175 - 599 V | 175 - 599 V | Average value: 328 V Grade Count:38 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 18.0 - 164 µm/m-°C | 10.0 - 91.0 µin/in-°F | Average value: 34.3 µm/m-°C Grade Count:43 |
| CTE, linear, Transverse to Flow | 60.0 - 90.0 µm/m-°C | 33.3 - 50.0 µin/in-°F | Average value: 79.7 µm/m-°C Grade Count:31 |
| Melting Point | 295 °C | 563 °F | Average value: 295 °C Grade Count:65 |
| Deflection Temperature at 0.46 MPa (66 psi) | 290 °C | 554 °F | Average value: 290 °C Grade Count:16 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 - 291 °C | 320 - 555 °F | Average value: 280 °C Grade Count:55 |
| Vicat Softening Point | 290 °C | 554 °F | Average value: 290 °C Grade Count:16 |
| Glass Transition Temp, Tg | 75.0 °C | 167 °F | Average value: 75.0 °C Grade Count:16 |
| UL RTI, Electrical | 130 - 140 °C | 266 - 284 °F | Average value: 139 °C Grade Count:16 |
| UL RTI, Mechanical with Impact | 110 - 125 °C | 230 - 257 °F | Average value: 117 °C Grade Count:16 |
| UL RTI, Mechanical without Impact | 110 - 130 °C | 230 - 266 °F | Average value: 122 °C Grade Count:16 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:37 |
| Oxygen Index | 22.0 - 37.0 % | 22.0 - 37.0 % | Average value: 29.5 % Grade Count:10 |
| Glow Wire Test | 650 - 960 °C | 1200 - 1760 °F | Average value: 869 °C Grade Count:11 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 293 - 321 °C | 560 - 610 °F | Average value: 308 °C Grade Count:13 |
| Mold Temperature | 79.4 - 149 °C | 175 - 300 °F | Average value: 117 °C Grade Count:13 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 86.2 MPa Grade Count:11 |