- 密度 [g/cm3]: 1.38
- 吸水率 [%]: 9.5
- 拉伸强度 [MPa]: 85.0
- 热变形温度 [℃]: 275.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 | ||
| Water Absorption | 9.5 % | 9.5 % | Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.6 % | 2.6 % | Humidity Absorption; Sim. to ISO 62 | ||
| Viscosity Test | 185 cm³/g | 185 cm³/g | Viscosity Number | ||
| Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm | 0.020 in/in | Normal; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | ISO 527-1/-2 | ||
| Elongation at Break | 20 % | 20 % | ISO 527-1/-2 | ||
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 3.60 GPa | 522 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 10.0 J/cm² @Temperature -30.0 °C | 47.6 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 10.0 J/cm² @Temperature 23.0 °C | 47.6 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -30.0 °C | 1.90 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.600 J/cm² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.5 @Frequency 1e+6 Hz | 3.5 @Frequency 1e+6 Hz | IEC 60250 | ||
| 3.8 @Frequency 100 Hz | 3.8 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.00050 @Frequency 100 Hz | 0.00050 @Frequency 100 Hz | IEC 60250 | ||
| 0.0020 @Frequency 1e+6 Hz | 0.0020 @Frequency 1e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 325 V | 325 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 20.0 °C | 44.4 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 20.0 °C | 50.0 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| Melting Point | 295 °C | 563 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 275 °C | 527 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 280 °C | 536 °F | 50°C/h 50N; ISO 306 | ||
| Glass Transition Temp, Tg | 75.0 °C | 167 °F | Glass Transition Temperature (10°C/min); ISO 11357-1/-2 | ||
| Flammability, UL94 | V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | IEC 60695-11-10 | ||
| V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | IEC 60695-11-10 | |||
| Oxygen Index | 29 % | 29 % | ISO 4589-1/-2 | ||
| Glow Wire Test | 825 °C @Thickness 3.00 mm | 1520 °F @Thickness 0.118 in | Glow Wire Ignition Temperature; IEC 60695-2-13 | ||
| 825 °C @Thickness 0.750 mm | 1520 °F @Thickness 0.0295 in | Glow Wire Ignition Temperature; IEC 60695-2-13 | |||
| 960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | Glow Wire Flammability Index; IEC 60695-2-12 | |||
| 960 °C @Thickness 0.750 mm | 1760 °F @Thickness 0.0295 in | Glow Wire Flammability Index; IEC 60695-2-12 | |||
| Descriptive Properties | |||||
| Flame Retardant | Yes | ||||
| Flame Retarding Agent | Yes | ||||
| Heat Stabilized or Stable to Heat | Yes | ||||
| Injection Molding | Yes | ||||
| Lubricants | Yes | ||||
| Platable | Yes | ||||
| Release Agent | Yes | ||||
| Without Fillers | Yes | ||||