- 密度 [g/cm3]: 1.25
- 吸水率 [%]: 11.4
- 拉伸强度 [MPa]: 90.0
- 热变形温度 [℃]: 290.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 | ||
| Water Absorption | 11.4 % | 11.4 % | Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 3.2 % | 3.2 % | Humidity Absorption; Sim. to ISO 62 | ||
| Viscosity Test | 180 cm³/g | 180 cm³/g | Viscosity Number | ||
| Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm | 0.020 in/in | Normal; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | ISO 527-1/-2 | ||
| Elongation at Break | 25 % | 25 % | ISO 527-1/-2 | ||
| Elongation at Yield | 10 % | 10 % | ISO 527-1/-2 | ||
| Tensile Modulus | 2.90 GPa | 421 ksi | ISO 527-1/-2 | ||
| Charpy Impact, Notched | 0.500 J/cm² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Comparative Tracking Index | 400 V | 400 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 20.0 °C | 44.4 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 20.0 °C | 55.6 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| Melting Point | 295 °C | 563 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 290 °C | 554 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 290 °C | 554 °F | 50°C/h 50N; ISO 306 | ||
| Glass Transition Temp, Tg | 75.0 °C | 167 °F | Glass Transition Temperature (10°C/min); ISO 11357-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695-11-10 | ||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | IEC 60695-11-10 | |||
| Descriptive Properties | |||||
| Heat Stabilized or Stable to Heat | Yes | ||||
| Injection Molding | Yes | ||||
| Platable | Yes | ||||
| Without Fillers | Yes | ||||