- 弯曲模量 [MPa]: 16.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.69 g/cc | 1.69 g/cc | ISO 1183 | ||
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h | ||
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 130 MPa | 18900 psi | |||
| Elongation at Yield | 1.0 % | 1.0 % | |||
| 1.2 % | 1.2 % | flexural | |||
| Modulus of Elasticity | 19.0 GPa | 2760 ksi | |||
| Flexural Strength | 185 MPa | 26800 psi | |||
| Flexural Modulus | 16.0 GPa | 2320 ksi | |||
| Charpy Impact Unnotched | 1.80 J/cm² | 8.57 ft-lb/in² | edgewise; ISO 179 1eU | ||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistance | <= 1.00e+6 ohm | <= 1.00e+6 ohm | |||
| Insulation Resistance | <= 1.00e+6 ohm | <= 1.00e+6 ohm | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 150 °C | 302 °F | |||
| 180 °C | 356 °F | short term | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 310 °C | 590 °F | mass temp | ||
| Nozzle Temperature | 280 - 330 °C | 536 - 626 °F | |||
| Zone 1 | 285 - 315 °C | 545 - 599 °F | |||
| Zone 2 | 305 - 315 °C | 581 - 599 °F | |||
| Zone 3 | 305 - 315 °C | 581 - 599 °F | |||
| Mold Temperature | 120 - 140 °C | 248 - 284 °F | |||
| Drying Temperature | 80.0 °C @Time 7200 - 43200 sec | 176 °F @Time 2.00 - 12.0 hour | Vacuum Dryer | ||
| 80.0 °C @Time 7200 - 28800 sec | 176 °F @Time 2.00 - 8.00 hour | Dehumidifying dryer | |||
| Descriptive Properties | |||||
| Color | natural color (black) | ||||