- 吸水率 [%]: 1.5
- 弯曲模量 [MPa]: 8.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ISO 1183 | ||
| Water Absorption | 1.5 % | 1.5 % | 23°C/24h | ||
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 165 MPa | 23900 psi | |||
| Elongation at Yield | 2.5 % | 2.5 % | |||
| 3.0 % | 3.0 % | flexural | |||
| Modulus of Elasticity | 10.0 GPa | 1450 ksi | |||
| Flexural Strength | 240 MPa | 34800 psi | |||
| Flexural Modulus | 8.00 GPa | 1160 ksi | |||
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | edgewise; ISO 179 1eU | ||
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | ISO 179 1eA | ||
| Coefficient of Friction, Dynamic | 0.31 | 0.31 | |||
| Coefficient of Friction, Static | 0.23 | 0.23 | |||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistance | >= 1.00e+9 ohm | >= 1.00e+9 ohm | |||
| Insulation Resistance | >= 1.00e+9 ohm | >= 1.00e+9 ohm | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 150 °C | 302 °F | |||
| 240 °C | 464 °F | short term | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | |||
| Vicat Softening Point | 290 °C | 554 °F | DIN ISO 306 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 310 °C | 590 °F | mass temp | ||
| Nozzle Temperature | 280 - 330 °C | 536 - 626 °F | |||
| Zone 1 | 285 - 315 °C | 545 - 599 °F | |||
| Zone 2 | 305 - 315 °C | 581 - 599 °F | |||
| Zone 3 | 305 - 315 °C | 581 - 599 °F | |||
| Mold Temperature | 120 - 140 °C | 248 - 284 °F | |||
| Drying Temperature | 80.0 °C @Time 7200 - 43200 sec | 176 °F @Time 2.00 - 12.0 hour | Vacuum Dryer | ||
| 80.0 °C @Time 7200 - 28800 sec | 176 °F @Time 2.00 - 8.00 hour | Dehumidifying dryer | |||
| Descriptive Properties | |||||
| Color | natural color (beige) | ||||