- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 1.27
- 吸水率 [%]: 0.4
- 弯曲强度 [MPa]: 140.0
- 弯曲模量 [MPa]: 7.20
- 热变形温度 [℃]: 245.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO R1183 |
| Water Absorption | 0.40 % | 0.40 % | 23°C / 24 hrs; ISO 62 |
| Moisture Absorption at Equilibrium | 1.0 % | 1.0 % | 23°C / 50% RH; ISO 62 |
| 2.3 % | 2.3 % | in 23°C water; ISO 62 | |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 235 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 455 °F | after drying; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 82 | 82 | ISO 868 |
| Tensile Strength, Ultimate | 140 MPa | 20300 psi | ISO R527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO R527 |
| Modulus of Elasticity | 8.80 GPa | 1280 ksi | ISO R527 |
| Flexural Strength | 190 MPa | 27600 psi | After conditioning at 23°C and 50% RH; ISO 178 |
| 210 MPa | 30500 psi | Dry; ISO 178 | |
| Flexural Modulus | 7.20 GPa | 1040 ksi | After conditioning at 23°C and 50% RH; ISO 178 |
| 7.60 GPa | 1100 ksi | Dry; ISO 178 | |
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | After conditioning at 23°C/50%RH; ISO 179/Af |
| 1.80 J/cm² @Temperature 23.0 °C | 8.57 ft-lb/in² @Temperature 73.4 °F | Dry; ISO 179/Af | |
| 17.0 J/cm² @Temperature -20.0 °C | 80.9 ft-lb/in² @Temperature -4.00 °F | Dry; ISO 179/Af | |
| 18.0 J/cm² @Temperature -20.0 °C | 85.7 ft-lb/in² @Temperature -4.00 °F | After conditioning at 23°C/50%RH; ISO 179/Af | |
| Tensile Creep Modulus, 1 hour | 7890 MPa | 1.14e+6 psi | ISO 899-1 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.10e+15 ohm-cm | 2.10e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 5.30e+15 ohm | 5.30e+15 ohm | ASTM D257 |
| Dielectric Strength | 34.0 kV/mm @Thickness 1.00 mm | 864 kV/in @Thickness 0.0394 in | ASTM D149 |
| Dissipation Factor | 0.016 @Frequency 100000 Hz | 0.016 @Frequency 100000 Hz | NFC 26 230 |
| 0.029 @Frequency 100 Hz | 0.029 @Frequency 100 Hz | NFC 26 230 | |
| 0.031 @Frequency 1000 Hz | 0.031 @Frequency 1000 Hz | NFC 26 230 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | NFC 26 220 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 18.0 µm/m-°C @Temperature 20.0 - 60.0 °C | 10.0 µin/in-°F @Temperature 68.0 - 140 °F | TMS2 Perkin Elmer |
| CTE, linear, Transverse to Flow | 110 µm/m-°C @Temperature 20.0 - 60.0 °C | 61.1 µin/in-°F @Temperature 68.0 - 140 °F | TMS2 Perkin Elmer |
| Melting Point | 255 °C | 491 °F | ISO R1218 |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | ISO R75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ISO R75 |
| Flammability, UL94 | HB | HB | |