- 吸水率 [%]: 1.7
- 缺口冲击强度: 1.3
- 拉伸强度 [MPa]: 135.0
- 弯曲模量 [MPa]: 6.30
- 硬度: 120.0
- 热变形温度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | Dry; ASTM D792 |
| Water Absorption | 1.7 % | 1.7 % | Wet |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | Dry; ASTM D2863 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | Dry; ASTM D2863 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 75 | 75 | Wet; ASTM D785 |
| 96 | 96 | Dry; ASTM D785 | |
| Hardness, Rockwell R | 120 | 120 | Dry; ASTM D785 |
| Tensile Strength, Yield | 135 MPa | 19600 psi | Wet; ASTM D638 |
| 210 MPa | 30500 psi | Dry; ASTM D638 | |
| Elongation at Break | 3.0 % | 3.0 % | Dry; ASTM D638 |
| 5.0 % | 5.0 % | Wet; ASTM D638 | |
| Flexural Strength | 210 MPa | 30500 psi | Wet; ASTM D790 |
| 325 MPa | 47100 psi | Dry; ASTM D790 | |
| Flexural Modulus | 6.30 GPa | 914 ksi | Wet; ASTM D790 |
| 10.4 GPa | 1510 ksi | Dry; ASTM D790 | |
| Izod Impact, Notched | 1.30 J/cm | 2.44 ft-lb/in | Dry; ASTM D256 |
| 1.70 J/cm | 3.18 ft-lb/in | Wet; ASTM D256 | |
| Taber Abrasion, mg/1000 Cycles | 15 | 15 | Wet; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 20.0 µm/m-°C @Temperature 20.0 °C | 11.1 µin/in-°F @Temperature 68.0 °F | Dry; ASTM D696 |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | Dry |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Dry; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | Dry; ASTM D648 |
| Flammability, UL94 | HB | HB | Dry |