- 吸水率 [%]: 1.3
- 缺口冲击强度: 1.4
- 拉伸强度 [MPa]: 170.0
- 弯曲模量 [MPa]: 9.80
- 硬度: 118.0
- 热变形温度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.58 g/cc | 1.58 g/cc | Dry; ASTM D792 |
| Water Absorption | 1.3 % | 1.3 % | Wet |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | Dry; ASTM D2863 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | Dry; ASTM D2863 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 80 | 80 | Wet; ASTM D785 |
| 95 | 95 | Dry; ASTM D785 | |
| Hardness, Rockwell R | 118 | 118 | Dry; ASTM D785 |
| Tensile Strength, Yield | 170 MPa | 24700 psi | Wet; ASTM D638 |
| 235 MPa | 34100 psi | Dry; ASTM D638 | |
| Elongation at Break | 2.5 % | 2.5 % | Dry; ASTM D638 |
| 4.0 % | 4.0 % | Wet; ASTM D638 | |
| Flexural Strength | 280 MPa | 40600 psi | Wet; ASTM D790 |
| 390 MPa | 56600 psi | Dry; ASTM D790 | |
| Flexural Modulus | 9.80 GPa | 1420 ksi | Wet; ASTM D790 |
| 14.5 GPa | 2100 ksi | Dry; ASTM D790 | |
| Izod Impact, Notched | 1.40 J/cm | 2.62 ft-lb/in | Dry; ASTM D256 |
| 1.90 J/cm | 3.56 ft-lb/in | Wet; ASTM D256 | |
| Taber Abrasion, mg/1000 Cycles | 22 | 22 | Wet; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 20.0 µm/m-°C @Temperature 20.0 °C | 11.1 µin/in-°F @Temperature 68.0 °F | Dry; ASTM D696 |
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | Dry |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Dry; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | Dry; ASTM D648 |
| Flammability, UL94 | HB | HB | Dry |