- 密度 [g/cm3]: 1.48
- 缺口冲击强度: 0.91
- 弯曲强度 [MPa]: 181.0
- 弯曲模量 [MPa]: 12.5
- 硬度: 121.0
- 热变形温度 [℃]: 265.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength, Ultimate | 181 MPa | 26300 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 268 MPa | 38900 psi | ASTM D790 |
| Flexural Modulus | 12.5 GPa | 1810 ksi | ASTM D790 |
| Izod Impact, Notched | 0.910 J/cm | 1.70 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.41 J/cm | 12.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 - 275 °C | 491 - 527 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 265 °C | 509 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 271 - 285 °C | 520 - 545 °F | Approximate middle barrel temperature range |