- 密度 [g/cm3]: 1.07
- 缺口冲击强度: 10.3
- 弯曲强度 [MPa]: 48.0
- 弯曲模量 [MPa]: 1.70
- 硬度: 106.0
- 热变形温度 [℃]: 97.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 106 | 106 | ASTM D785 |
| Tensile Strength, Ultimate | 48.0 MPa | 6960 psi | ASTM D638 |
| Elongation at Break | 138 % | 138 % | ASTM D638 |
| Flexural Strength | 69.0 MPa | 10000 psi | ASTM D790 |
| Flexural Modulus | 1.70 GPa | 247 ksi | ASTM D790 |
| Izod Impact, Notched | 10.3 J/cm | 19.3 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 - 275 °C | 491 - 527 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C | 207 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 285 - 302 °C | 545 - 576 °F | Approximate middle barrel temperature range |