A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced, Heat Stabilized 66物性表参数

A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced, Heat Stabilized 66

A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced, Heat Stabilized 66 物性表: A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced, Heat Stabilized 66物性表及特性介绍,A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced, Heat Stabilized 66注塑参数详情,如需A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced, Heat Stabilized 66下载, 可到相关下载区下载

热变形温度 [℃]: 250.0

Physical Properties	Metric	English	Comments

Specific Gravity	1.57 g/cc	1.57 g/cc	ISO 1183/1
Linear Mold Shrinkage	0.0010 cm/cm @Thickness 3.175 mm	0.0010 in/in @Thickness 0.1250 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	230 MPa	33400 psi	ISO 527
Tensile Modulus	16.0 GPa	2320 ksi	ISO 527

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	250 °C	482 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	250 °C	482 °F	ISO 75

Processing Properties	Metric	English	Comments
Melt Temperature	290 - 310 °C	554 - 590 °F
Mold Temperature	65.6 - 93.3 °C	150 - 200 °F
Drying Temperature	79.4 °C	175 °F
Dry Time	2 - 4 hour	2 - 4 hour	Predrying

关键词:
供应
PA66
A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced
Heat Stabilized 66

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-44983.html

免责声明: 本文 A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced, Heat Stabilized 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息